Study on electron beam welding process of the first wall of water-cooled ceramic breeder (WCCB) blanket
文献类型：期刊论文
| 作者 | Zhang, Yong1,2 ; Wu, Jiefeng1,4; Liu, Zhihong1,4; Liu, Songlin1; Lei, Mingzhun1; Wang, Wanjing1; Atif, Muhammad3; Liu, Zhenfei1,4; Ma, Jianguo1,4
|
| 刊名 | FUSION ENGINEERING AND DESIGN
 |
| 出版日期 | 2021-12-01 |
| 卷号 | 173 |
| 关键词 | Electron beam welding Blanket First wall Mechanical properties Welding technology |
| ISSN号 | 0920-3796 |
| DOI | 10.1016/j.fusengdes.2021.112927 |
| 通讯作者 | Ma, Jianguo(mjg@ipp.ac.cn) |
| 英文摘要 | Water- cooled ceramic breeder (WCCB) blanket is one of the candidate blanket for China Fusion Engineering Test Reactor (CFETR) independently developed by China Institute of plasma physics. The first wall (FW) is a component of WCCB, which directly faces the plasma. FW contains flow channels and has complex shape structure, therefore, it is difficult to complete the full-scale manufacturing by one kind of welding process. Hence, in the development process, the components of FW are first connected by hot isostatic pressing (HIP), and then connected by electron beam welding (EBW), so as to form the full-scaled FW connection. In this paper, the EBW process of FW was studied. The results showed that when the electron beam current was 50 mA and the focus was on the surface, the welded joint with 20 mm penetration and good shape can be formed. After the one time welding and the twice welding (overlapping first welding) of the weld, the tensile test fracture occurred in the base metal. The impact energy of the one time welding was 13 MPa, 18 MPa, and 21 MPa, respectively, and the impact energy of the twice welding was 19 MPa, 20 MPa, and 51 MPa, respectively. The microstructure of the joint was composed of delta-ferrite and lath martensite. When the weld penetration was increased to 50 mm, the lower the focus is, the smaller the porosity at the bottom of the weld is. Similarly, when the lower focus was used, the porosity at the bottom of the weld disappeared basically; The EBW test on the scaled FW with W/Cu sheets showed that when the we took the test pieces with the W-Cu sheet spacing is 4 mm, the welded joint with good surface shape and no internal defects can be formed without scanning deflection electron beam welding, and ultrasonic testing showed that EBW does not affect on the HIP interface. This provides a favorable basis for the future test of equal ratio FW test piece and the welding of actual FW. |
| WOS关键词 | CONCEPTUAL DESIGN |
| 资助项目 | National Key R&D Program of China[2017YFE03004] ; National Key R&D Program of China[2017YFE03003] |
| WOS研究方向 | Nuclear Science & Technology |
| 语种 | 英语 |
| WOS记录号 | WOS:000722687300005 |
| 出版者 | ELSEVIER SCIENCE SA |
| 资助机构 | National Key R&D Program of China |
| 源URL | [http://ir.hfcas.ac.cn:8080/handle/334002/126748]  |
| 专题 | 中国科学院合肥物质科学研究院 |
| 通讯作者 | Ma, Jianguo |
| 作者单位 | 1.Chinese Acad Sci, Hefei Inst Phys Sci, Inst Plasma Phys, Hefei 230031, Peoples R China 2.Univ Sci & Technol China, Hefei 230026, Peoples R China 3.Univ Siegen, Dept Chem, Macromol Chem, Adolf Reichwein Str 2, D-57076 Siegen, Germany 4.Anhui Prov Key Lab Special Welding Technol, Huainan 232000, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, Yong,Wu, Jiefeng,Liu, Zhihong,et al. Study on electron beam welding process of the first wall of water-cooled ceramic breeder (WCCB) blanket[J]. FUSION ENGINEERING AND DESIGN,2021,173. |
| APA | Zhang, Yong.,Wu, Jiefeng.,Liu, Zhihong.,Liu, Songlin.,Lei, Mingzhun.,...&Ma, Jianguo.(2021).Study on electron beam welding process of the first wall of water-cooled ceramic breeder (WCCB) blanket.FUSION ENGINEERING AND DESIGN,173. |
| MLA | Zhang, Yong,et al."Study on electron beam welding process of the first wall of water-cooled ceramic breeder (WCCB) blanket".FUSION ENGINEERING AND DESIGN 173(2021). |
入库方式： OAI收割
来源：合肥物质科学研究院
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。