Effects of pH and Cl- concentration on corrosion behavior of the galvanized steel in simulated rust layer solution
文献类型：期刊论文
| 作者 | Liu, Shuan1,2; Sun, Huyuan1 ; Sun, Lijuan1; Fan, Huiji1,2
|
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2012-12-01 |
| 卷号 | 65页码:520-527 |
| 关键词 | Rust EIS Pitting corrosion |
| ISSN号 | 0010-938X |
| 通讯作者 | Sun, HY (reprint author), Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China. |
| 英文摘要 | Effects of pH and Cl- concentration on the corrosion behavior of galvanized steel in simulated rust layer (SRL) solution have been investigated using measurements of weight loss, electrochemical impedance spectroscopy (EIS), linear polarization combined with cyclic polarization experiment. In neutral SRL solutions, pitting corrosion occurred on the galvanized steel simultaneously. However, exposure to high alkaline solutions resulted in passivation. Results revealed that the galvanized steel in SRL solution was susceptible to pitting corrosion in all chloride solution of concentration ranging between 0.1 and 0.6 M. (C) 2012 Elsevier Ltd. All rights reserved. |
| 学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 收录类别 | SCI |
| 原文出处 | 10.1016/j.corsci.2012.08.056 |
| 语种 | 英语 |
| WOS记录号 | WOS:000311192800056 |
| 公开日期 | 2013-09-24 |
| 源URL | [http://ir.qdio.ac.cn/handle/337002/12318]  |
| 专题 | 海洋研究所_实验海洋生物学重点实验室 海洋研究所_海洋腐蚀与防护研究发展中心 |
| 作者单位 | 1.Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China 2.Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu, Shuan,Sun, Huyuan,Sun, Lijuan,et al. Effects of pH and Cl- concentration on corrosion behavior of the galvanized steel in simulated rust layer solution[J]. CORROSION SCIENCE,2012,65:520-527. |
| APA | Liu, Shuan,Sun, Huyuan,Sun, Lijuan,&Fan, Huiji.(2012).Effects of pH and Cl- concentration on corrosion behavior of the galvanized steel in simulated rust layer solution.CORROSION SCIENCE,65,520-527. |
| MLA | Liu, Shuan,et al."Effects of pH and Cl- concentration on corrosion behavior of the galvanized steel in simulated rust layer solution".CORROSION SCIENCE 65(2012):520-527. |