Enhancement of multi-pass weld-crack resistance of Co-based superalloys by B-doping
文献类型：期刊论文
| 作者 | Wen, Mingyue2,3; Sun, Yuan3; Yu, Jinjiang3; Meng, Jie3; Wang, Shiyang3; Dong, Zhiguo1; Niu, Juntao1; Sun, Xiaofeng3; Zhou, Yizhou3 |
| 刊名 | MATERIALS CHARACTERIZATION
 |
| 出版日期 | 2021-12-01 |
| 卷号 | 182页码:10 |
| 关键词 | Weld-crack resistance Co-based superalloy B-doping Fusion welding Weldability |
| ISSN号 | 1044-5803 |
| DOI | 10.1016/j.matchar.2021.111527 |
| 通讯作者 | Yu, Jinjiang(jjyu@imr.ac.cn) ; Meng, Jie(jmeng@imr.ac.cn) |
| 英文摘要 | Enhancing weld-crack resistance of Co-based suerpalloys is of both scientific and practical significance. In this work, the fusion zone weld-crack resistance of Co-9.2Al-9 W-xB (at.%, x = 0, 0.05, 0.20) superalloys during multi-pass fusion welding is investigated. It is found that weld cracks form in fusion zone without B-doping and with B-doping of 0.20%. However, no cracks form in the welded superalloy with 0.05% B alloys, suggesting the weld-crack resistance of Co-based superalloys can be enhanced by a small amount of B-doping. The mechanisms underlying the different weldability of the three Co-based superalloys are clarified. With B-doping of 0.05 at.%, the precipitation of mu-Co7W6 phase on grain boundaries can be fully suppressed, and the internal residual stress is largely reduced. The suppression of precipitated phases and low internal stress in the superalloy with 0.05% B doping account for its much enhanced weld-crack resistance. However, with further B-doping of 0.20%, the M3B2 phase precipitates on the grain boundaries and the internal stress inside grains also increases, which account for the further deterioration of weldabilty. These findings are believed to promote the development of Co-based superalloys with high weld-crack resistance. |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000711216000003 |
| 出版者 | ELSEVIER SCIENCE INC |
| 源URL | [http://ir.imr.ac.cn/handle/321006/167113]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Yu, Jinjiang; Meng, Jie |
| 作者单位 | 1.AVIC Shenyang Engine Design & Res Inst, Shenyang 110015, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wen, Mingyue,Sun, Yuan,Yu, Jinjiang,et al. Enhancement of multi-pass weld-crack resistance of Co-based superalloys by B-doping[J]. MATERIALS CHARACTERIZATION,2021,182:10. |
| APA | Wen, Mingyue.,Sun, Yuan.,Yu, Jinjiang.,Meng, Jie.,Wang, Shiyang.,...&Zhou, Yizhou.(2021).Enhancement of multi-pass weld-crack resistance of Co-based superalloys by B-doping.MATERIALS CHARACTERIZATION,182,10. |
| MLA | Wen, Mingyue,et al."Enhancement of multi-pass weld-crack resistance of Co-based superalloys by B-doping".MATERIALS CHARACTERIZATION 182(2021):10. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。