Suppressing the compositional non-uniformity of AlGaN grown on a HVPE-AlN template with large macro-steps
文献类型：期刊论文
| 作者 | K.Jiang; X.J.Sun; J.W.Ben; Z.M.Shi; Y.P.Jia; Y.Wu; C.H.Kai |
| 刊名 | Crystengcomm
 |
| 出版日期 | 2019 |
| 卷号 | 21期号:33页码:4864-4873 |
| 关键词 | potential fluctuations,gan films,alxga1-xn,sapphire,quality,localization,relaxation,inversion |
| ISSN号 | 1466-8033 |
| DOI | 10.1039/c9ce00608g |
| 英文摘要 | AlGaN is a promising material for ultraviolet optoelectronic and microelectronic devices. In this report, we investigated the influences of metallization pretreatment on the strain, morphology and optical properties of AlGaN grown on HVPE-AlN. The results indicated that the pretreatment could effectively alleviate the compressive strain from HVPE-AlN and thus lower the Al-content in AlGaN. The composition pulling effect was considered to be responsible for the Al-content reduction. On the other hand, the pretreatment could help to improve the surface morphology of AlGaN, which was attributed to the growth mode transition involved in the pretreatment. Besides, the optical measurements revealed that the AlGaN directly grown on HVPE-AlN exhibited distinct compositional non-uniformity and the reasons were the macro-steps in the surface of HVPE-AlN and the mobility discrepancy of Al and Ga atoms. The pretreatment could eliminate such non-uniformity effectively. The carbon clusters formed by metal-organic decomposition during the pretreatment were believed to be responsible for the improvement. The localized excitonic characteristics were also studied. It was found that the localized excitonic states were abundant and energy transport processes were complex in AlGaN directly grown on HVPE-AlN, which would result in undesired light emissions. The pretreatment was proved to be effective in optimizing the localized excitonic characteristics, which may be attributed to the alleviation of Al-content fluctuation by the pretreatment. These results can not only provide a deeper understanding of AlGaN epitaxy, but also offer an approach to optimize the properties of the AlGaN materials. |
| URL标识 | 查看原文 |
| 语种 | 英语 |
| 源URL | [http://ir.ciomp.ac.cn/handle/181722/63305]  |
| 专题 | 中国科学院长春光学精密机械与物理研究所 |
| 推荐引用方式 GB/T 7714 | K.Jiang,X.J.Sun,J.W.Ben,et al. Suppressing the compositional non-uniformity of AlGaN grown on a HVPE-AlN template with large macro-steps[J]. Crystengcomm,2019,21(33):4864-4873. |
| APA | K.Jiang.,X.J.Sun.,J.W.Ben.,Z.M.Shi.,Y.P.Jia.,...&C.H.Kai.(2019).Suppressing the compositional non-uniformity of AlGaN grown on a HVPE-AlN template with large macro-steps.Crystengcomm,21(33),4864-4873. |
| MLA | K.Jiang,et al."Suppressing the compositional non-uniformity of AlGaN grown on a HVPE-AlN template with large macro-steps".Crystengcomm 21.33(2019):4864-4873. |
入库方式： OAI收割
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。