High-Performance Planar-Type Ultraviolet Photodetector Based on High-Quality CH3NH3PbCl3 Perovskite Single Crystals
文献类型：期刊论文
| 作者 | Z.Cheng; K.W.Liu; J.L.Yang; X.Chen; X.H.Xie; B.H.Li; Z.Z.Zhang |
| 刊名 | Acs Applied Materials & Interfaces
 |
| 出版日期 | 2019 |
| 卷号 | 11期号:37页码:34144-34150 |
| 关键词 | CH3NH3PbCl3,perovskite,photodetectors,single crystals,high speed,ray-diffraction |
| ISSN号 | 1944-8244 |
| DOI | 10.1021/acsami.9b09035 |
| 英文摘要 | A hybrid perovskite MAPbCl(3) (MA = CH3NH3+) single crystal is considered to be one of the most viable candidates for the development of photodetectors because of its outstanding optoelectronic properties. However, the relatively lower crystalline quality of the reported MAPbCl(3) single crystals fabricated by the traditional one-step inverse temperature crystallization results in momentous degradation in the performance of their photodetectors. Here, we present a novel two-step temperature process to fabricate high-quality MAPbCl(3) single crystals, namely, lower temperature nucleation and higher temperature crystallization. These MAPbCl(3) single crystals present low defect density (similar to 7.9 x 10(9) cm(-3)) commensurate with the best-quality crystals of hybrid organic-inorganic lead halide perovskites reported so far. Moreover, a high-performance ultraviolet photodetector was demonstrated on MAPbCl(3) single crystals. At 30 V, the peak responsivity at 415 nm of the photodetector is as high as 3.73 A W-1 (light intensity = 1 mW cm(-2)), similar to 2-3 orders of magnitude higher than that of the previously reported MAPbCl(3) photodetectors. Meanwhile, the device has an ultrafast response speed with a rise time of 130 ns, which is one of the shortest values of MAPbX(3)-based photodetectors. Our findings open a new way to obtain high-quality perovskite single crystals and their high-performance photodetectors. |
| URL标识 | 查看原文 |
| 语种 | 英语 |
| 源URL | [http://ir.ciomp.ac.cn/handle/181722/63432]  |
| 专题 | 中国科学院长春光学精密机械与物理研究所 |
| 推荐引用方式 GB/T 7714 | Z.Cheng,K.W.Liu,J.L.Yang,et al. High-Performance Planar-Type Ultraviolet Photodetector Based on High-Quality CH3NH3PbCl3 Perovskite Single Crystals[J]. Acs Applied Materials & Interfaces,2019,11(37):34144-34150. |
| APA | Z.Cheng.,K.W.Liu.,J.L.Yang.,X.Chen.,X.H.Xie.,...&Z.Z.Zhang.(2019).High-Performance Planar-Type Ultraviolet Photodetector Based on High-Quality CH3NH3PbCl3 Perovskite Single Crystals.Acs Applied Materials & Interfaces,11(37),34144-34150. |
| MLA | Z.Cheng,et al."High-Performance Planar-Type Ultraviolet Photodetector Based on High-Quality CH3NH3PbCl3 Perovskite Single Crystals".Acs Applied Materials & Interfaces 11.37(2019):34144-34150. |
入库方式： OAI收割
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。