Microstructure and temperature-dependence of Raman scattering properties of beta-(AlxGa1-x)(2)O-3 crystals

文献类型:期刊论文

作者X. Chen,W. L. Niu,L. Y. Wan,C. T. Xia,H. Y. Cui,D. N. Talwar and Z. C. Feng
刊名Superlattices and Microstructures
出版日期2020
卷号140页码:9
ISSN号0749-6036
DOI10.1016/j.spmi.2020.106469
英文摘要Bulk crystals of beta-Ga2O3, (Al0.1Ga0.9)(2)O-3 and (Al0.2Ga0.8)(2)O-3 were grown by the optical floating zone and edge-defined film-fed methods. Their microstructure and temperature-dependent phonon characteristics were investigated systematically by using high resolution X-ray diffraction (HR-XRD) and Raman scattering spectroscopy. HR-XRD results revealed a very good crystalline phase for all the samples. As compared to the pure beta-Ga2O3, the interplanar spacings in (Al0.1Ga0.9)(2)O-3 and (Al0.2Ga0.8)(2)O-3 samples are found decreasing with the increase of Al contents - exhibiting distorted lattice structures. Due to the deformations in (AlxGa1-x)(2)O-3, the Raman peaks revealed redshifts and linewidth broadening as the Al composition (x) is increased. The lattice distortion mainly affected the Raman modes in the range of less than 600 cm(-1) and had a relatively trivial effect on the modes higher than 600 cm(-1). With the increase of temperature, the Raman peaks are also redshifted and linewidth broadened. Similar to a pure beta-Ga2O3, our Raman shifts in the two (AlxGa1-x)(2)O-3 crystals revealed quadratic dependence on temperature - showing specific relationships. However, the temperature dependent widening of the Raman active phonons in (AlxGa1-x)(2)O-3 exhibited a convoluted behavior different from beta-Ga2O3. The results are significant for further understanding of (AlxGa1-x)(2)O-3 crystals and evaluating its use in device applications.
URL标识查看原文
语种英语
源URL[http://ir.ciomp.ac.cn/handle/181722/64683]  
专题中国科学院长春光学精密机械与物理研究所
推荐引用方式
GB/T 7714
X. Chen,W. L. Niu,L. Y. Wan,C. T. Xia,H. Y. Cui,D. N. Talwar and Z. C. Feng. Microstructure and temperature-dependence of Raman scattering properties of beta-(AlxGa1-x)(2)O-3 crystals[J]. Superlattices and Microstructures,2020,140:9.
APA X. Chen,W. L. Niu,L. Y. Wan,C. T. Xia,H. Y. Cui,D. N. Talwar and Z. C. Feng.(2020).Microstructure and temperature-dependence of Raman scattering properties of beta-(AlxGa1-x)(2)O-3 crystals.Superlattices and Microstructures,140,9.
MLA X. Chen,W. L. Niu,L. Y. Wan,C. T. Xia,H. Y. Cui,D. N. Talwar and Z. C. Feng."Microstructure and temperature-dependence of Raman scattering properties of beta-(AlxGa1-x)(2)O-3 crystals".Superlattices and Microstructures 140(2020):9.

入库方式: OAI收割

来源:长春光学精密机械与物理研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。