Measurement on the desorption yields of ceramic and Au-coated ceramic irradiated with Bi32+and Xe23+
文献类型：期刊论文
| 作者 | Xie, W. J.1,2,3; Meng, J.2,3,4 ; Li, C. C.2,4; Jiao, J. Q.2; Chai, Z.2,4; Luo, C.1,2,3,4; Yang, W. S.2,3,4; Shen, G. D.2,3; Li, Z. S.2,3; Zhou, D. T.2
|
| 刊名 | VACUUM
 |
| 出版日期 | 2021-12-01 |
| 卷号 | 194页码:7 |
| ISSN号 | 0042-207X |
| 关键词 | HIAF Desorption yields Ceramic Beam cleaning effect |
| DOI | 10.1016/j.vacuum.2021.110636 |
| 通讯作者 | Meng, J.(mengjun@impcas.ac.cn) |
| 英文摘要 | The Booster Ring (BRing) is the key part of the High Intensity Heavy Ion Accelerator Facility (HIAF). In order to reduce the eddy current effect, specifically developed stainless steel vacuum chambers with ultra-thin (0.3 mm) walls and ceramic spacers will be used. Desorption yields experiments were carried out on spacers made of zirconia ceramic, on zirconia ceramic coated with different Au thicknesses and coating processes, as well as on zirconia ceramic coated with getter films. A dedicated mass spectrometer was used to analyze the changes in the gas composition during the bombardment. The results show that Au-coated zirconia ceramic can effectively lower the desorption yields, the higher the Au coating thickness, the lower the desorption yield. When the beam impinges on the surface of the zirconia ceramic, the pressure randomly fluctuates, without showing any clear long term beam cleaning effect. As far as the coating process is concerned, samples coated by magnetron sputtering show higher desorption yields than those electroplated. However, the electroplating process is characterized by a low bonding force between the films and the ceramic substrate, which makes possible for the film to peel off under beam bombardment. Finally, TiN-coated zirconia ceramic has better static vacuum performances. However, due to its strong H2 absorption capacity, TiN coated samples will release more H2 under bombardment, thus providing a worse dynamic vacuum conditions. Practical consequences for the BRing vacuum system of the HIAF are given. |
| WOS研究方向 | Materials Science ; Physics |
| 语种 | 英语 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| WOS记录号 | WOS:000705986500001 |
| 源URL | [http://119.78.100.186/handle/113462/136186]  |
| 专题 | 中国科学院近代物理研究所 |
| 通讯作者 | Meng, J. |
| 作者单位 | 1.Lanzhou Univ Technol, Sch Petrochem Engn, Lanzhou 730050, Peoples R China 2.Chinese Acad Sci, Inst Modern Phys, Lanzhou 730000, Peoples R China 3.Huizhou Res Ctr Ion Sci, Huizhou 516003, Peoples R China 4.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Xie, W. J.,Meng, J.,Li, C. C.,et al. Measurement on the desorption yields of ceramic and Au-coated ceramic irradiated with Bi32+and Xe23+[J]. VACUUM,2021,194:7. |
| APA | Xie, W. J..,Meng, J..,Li, C. C..,Jiao, J. Q..,Chai, Z..,...&Li, C..(2021).Measurement on the desorption yields of ceramic and Au-coated ceramic irradiated with Bi32+and Xe23+.VACUUM,194,7. |
| MLA | Xie, W. J.,et al."Measurement on the desorption yields of ceramic and Au-coated ceramic irradiated with Bi32+and Xe23+".VACUUM 194(2021):7. |
入库方式： OAI收割
来源：近代物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。