Tensile properties of Ti-48Al-2Cr-2Nb alloy having similarly oriented lamellae with fine lamellar spacing facilitated by suction casting
文献类型：期刊论文
| 作者 | Xia, Zhizhou1,2; Cui, Yuyou2; Shen, Yingying2; Arroussi, Mohammed1,2; Liu, Ronghua2; Yang, Liang2; Jia, Qing2; Yang, Rui2 |
| 刊名 | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
 |
| 出版日期 | 2022-01-07 |
| 卷号 | 830页码:11 |
| 关键词 | TiAl alloy Oriented lamellar microstructure Lamellar spacing Tensile properties Fracture behavior |
| ISSN号 | 0921-5093 |
| DOI | 10.1016/j.msea.2021.142303 |
| 通讯作者 | Yang, Rui(ryang@imr.ac.cn) |
| 英文摘要 | Ti-48Al-2Cr-2Nb (at. pet) billet was prepared by suction casting into a cold steel mould, and its microstructures and mechanical properties at room and elevated temperatures were investigated. The billet featured lamellar microstructure with refined colony sizes, fine interlamellar spacing, and lamellar interfaces nearly parallel to the mould surface with a scatter angle within 30 degrees. Benefitting from this microstructure, the billet showed excellent mechanical properties at temperatures up to 850 degrees C, with yield strength of 629 +/- 29 MPa at ambient temperature, 549 +/- 14 MPa at 650 degrees C, 565 +/- 17 MPa at 700 degrees C, 475 +/- 6 MPa at 800 degrees C and 413 +/- 9 MPa at 850 degrees C, comparable to that of the third-generation TiAl alloys like TNM but much superior to that of most reported cast Ti-48Al-2Cr-2Nb alloys. The total fracture elongation at room temperature and 700 degrees C were (1.8 +/- 0.2) % and (15.9 +/- 3.5) %, respectively. Although the fracture at 700 degrees C occurred in a brittle mode, the tensile samples possessed ductile tensile elongation. |
| WOS研究方向 | Science & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000730159200003 |
| 出版者 | ELSEVIER SCIENCE SA |
| 源URL | [http://ir.imr.ac.cn/handle/321006/167322]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Yang, Rui |
| 作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230022, Peoples R China 2.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Xia, Zhizhou,Cui, Yuyou,Shen, Yingying,et al. Tensile properties of Ti-48Al-2Cr-2Nb alloy having similarly oriented lamellae with fine lamellar spacing facilitated by suction casting[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2022,830:11. |
| APA | Xia, Zhizhou.,Cui, Yuyou.,Shen, Yingying.,Arroussi, Mohammed.,Liu, Ronghua.,...&Yang, Rui.(2022).Tensile properties of Ti-48Al-2Cr-2Nb alloy having similarly oriented lamellae with fine lamellar spacing facilitated by suction casting.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,830,11. |
| MLA | Xia, Zhizhou,et al."Tensile properties of Ti-48Al-2Cr-2Nb alloy having similarly oriented lamellae with fine lamellar spacing facilitated by suction casting".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 830(2022):11. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。