Corrosion behaviour of 316 stainless steel in NaCl-KCl-MgCl2 salt vapour at 700 degrees C
文献类型：期刊论文
| 作者 | Liu, Qi; Xu, Hongxia; Yin, Huiqin; Li, Na; Wang, Wenrui; Li, Linfan; Tang, Zhongfeng; Qian, Yuan |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2021-11 |
| 卷号 | 194 |
| ISSN号 | 0010-938X |
| DOI | 10.1016/j.corsci.2021.109921 |
| 英文摘要 | The corrosion behaviour of 316 stainless steel in NaCl-KCl-MgCl2 salt vapour at 700 degrees C under static conditions was investigated in this experiment. Easy-to-peel oxide layers were formed on the surface, and their composition and structure changed as exposure continued. The initially formed oxide monolayer was gradually transformed into oxide multilayers, and the outermost layer changed from Cr-Fe oxide to Mg-Cr oxide. The evolution of surface oxide layers was due to the varying diffusion rates of elements in 316 stainless steel as well as to the differing reaction rate of MgCl2 in the salt vapour. |
| 源URL | [http://ir.isl.ac.cn/handle/363002/34594]  |
| 专题 | 青海盐湖研究所_盐湖资源与化学实验室 |
| 推荐引用方式 GB/T 7714 | Liu, Qi,Xu, Hongxia,Yin, Huiqin,et al. Corrosion behaviour of 316 stainless steel in NaCl-KCl-MgCl2 salt vapour at 700 degrees C[J]. CORROSION SCIENCE,2021,194. |
| APA | Liu, Qi.,Xu, Hongxia.,Yin, Huiqin.,Li, Na.,Wang, Wenrui.,...&Qian, Yuan.(2021).Corrosion behaviour of 316 stainless steel in NaCl-KCl-MgCl2 salt vapour at 700 degrees C.CORROSION SCIENCE,194. |
| MLA | Liu, Qi,et al."Corrosion behaviour of 316 stainless steel in NaCl-KCl-MgCl2 salt vapour at 700 degrees C".CORROSION SCIENCE 194(2021). |
入库方式： OAI收割
来源：青海盐湖研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。