Highly ductile hypereutectic Al-Si alloys fabricated by selective laser melting
文献类型：期刊论文
| 作者 | Yang, Yafeng1,2; Geng, Kang1,2; Li, Shaofu1,2; Bermingham, Michael3; Misra, R. D. K.4 |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2022-05-30 |
| 卷号 | 110页码:84-95 |
| 关键词 | Al -Si alloys Heterogeneous nucleation Ductility Powder processing Selective laser melting |
| ISSN号 | 1005-0302 |
| DOI | 10.1016/j.jmst.2021.07.050 |
| 英文摘要 | In the endeavor to maximize the refinement effect of primary Si and alleviate the inherent brittleness of hypereutectic Al-Si alloy, the approach of coating P as a modifier on powder was adopted. The ulti-mate aim was to create more heterogeneous fine AlP nucleus and enhance the nucleation efficiency of primary Si on AlP to refine the coarse primary Si to nano-scale during 3D printing. In the combination of large undercooling and high density of nucleation sites, the size of primary Si was successfully refined to 20 0-30 0 nm and the divorced eutectic was also induced to modify the microstructure of matrix. In the presence of nano-scale primary Si, the melting pool boundary (MPB) feature disappeared and the fracture mechanism also changed from load transfer to interfacial fracture. Compared with the pristine alloy, the ductility was increased four times without significantly changing the ultimate tensile strength (UTS) and wear resistance. The improvement of ductility is attributed to the refinement of primary Si, the disappearance of MPB features and the formation of divorced eutectic. The optimal tensile properties were: UTS-482 MPa, yield strength-320 MPa and ductility of 8.1% at 0.05 wt.% P. These are comparable to those for high-strength Al alloys. (c) 2021 Published by Elsevier Ltd on behalf of Chinese Society for Metals. |
| WOS关键词 | MECHANICAL-PROPERTIES ; HEAT-TREATMENT ; TENSILE PROPERTIES ; GRAIN-REFINEMENT ; MELTED ALSI10MG ; AL-50SI ALLOY ; MICROSTRUCTURE ; ALUMINUM ; EVOLUTION ; PARTICLES |
| 资助项目 | National Key Research and Development Program of China[2018YFB1105100] ; Scientific Instrument Developing Project of the Chinese Academy of Sciences[YJKYYQ20190011] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000788148800001 |
| 出版者 | JOURNAL MATER SCI TECHNOL |
| 资助机构 | National Key Research and Development Program of China ; Scientific Instrument Developing Project of the Chinese Academy of Sciences |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/52887]  |
| 专题 | 中国科学院过程工程研究所 |
| 通讯作者 | Yang, Yafeng |
| 作者单位 | 1.Chinese Acad Sci, Inst Proc Engn, State Key Lab Multiphase Complex Syst, Beijing 100190, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 3.Univ Queensland, Sch Mech & Min Engn, St Lucia, Qld 4072, Australia 4.Univ Texas El Paso, Dept Met Mat & Biomed Engn, 500 W Univ Ave, El Paso, TX 79968 USA |
| 推荐引用方式 GB/T 7714 | Yang, Yafeng,Geng, Kang,Li, Shaofu,et al. Highly ductile hypereutectic Al-Si alloys fabricated by selective laser melting[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2022,110:84-95. |
| APA | Yang, Yafeng,Geng, Kang,Li, Shaofu,Bermingham, Michael,&Misra, R. D. K..(2022).Highly ductile hypereutectic Al-Si alloys fabricated by selective laser melting.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,110,84-95. |
| MLA | Yang, Yafeng,et al."Highly ductile hypereutectic Al-Si alloys fabricated by selective laser melting".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 110(2022):84-95. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。