The corrosion behavior and cracking susceptibility of the disbonded coating in the X80 steel pipeline by theoretical simulations and experimental measurements
文献类型:期刊论文
作者 | Zhao, Bo3; Zhao, Zhijuan3; Jin, Dong3; Li, Na2; Liu, Linlin2; Cao, Xin1; Shou, Binan3 |
刊名 | CORROSION REVIEWS |
出版日期 | 2021-12-01 |
卷号 | 39期号:6页码:573-587 |
ISSN号 | 0334-6005 |
关键词 | coating corrosion in-situ electrochemical testing pipeline steel |
DOI | 10.1515/corrrev-2021-0013 |
英文摘要 | The corrosion behavior and cracking suscepti-bility of the disbonded coating in the X80 steel pipeline were investigated by different methods. The oxygen con -tent in the trapped solution decreased rapidly with the formation of an airtight disbonded area. The airtight system affected the electrode reaction process, resulting in the inhibition of corrosion in the center of the disbonded area and the more refined surface finish of the sample. The bottom of the disbonded area underwent a relatively intense and accelerated corrosion reaction controlled by the diffusion process. The cracking susceptibility of the X80 steel firstly decreased and then increased in the pointing direction. |
WOS关键词 | STRESS-CORROSION ; CATHODIC PROTECTION ; CREVICE CORROSION ; ELECTROCHEMICAL-BEHAVIOR ; CYCLIC STRESS ; CARBON-STEEL ; E690 STEEL ; X70 ; HYDROGEN ; MODEL |
资助项目 | China Special Equipment Inspection and Research Institute for Youth Foundation[2019-02] ; China Special Equipment Inspection and Research Institute for Youth Foundation[2018-11] ; National Natural Science Foundation of China[51801226] |
WOS研究方向 | Electrochemistry ; Metallurgy & Metallurgical Engineering ; Materials Science |
语种 | 英语 |
出版者 | WALTER DE GRUYTER GMBH |
WOS记录号 | WOS:000726739900005 |
资助机构 | China Special Equipment Inspection and Research Institute for Youth Foundation ; China Special Equipment Inspection and Research Institute for Youth Foundation ; National Natural Science Foundation of China ; National Natural Science Foundation of China ; China Special Equipment Inspection and Research Institute for Youth Foundation ; China Special Equipment Inspection and Research Institute for Youth Foundation ; National Natural Science Foundation of China ; National Natural Science Foundation of China ; China Special Equipment Inspection and Research Institute for Youth Foundation ; China Special Equipment Inspection and Research Institute for Youth Foundation ; National Natural Science Foundation of China ; National Natural Science Foundation of China ; China Special Equipment Inspection and Research Institute for Youth Foundation ; China Special Equipment Inspection and Research Institute for Youth Foundation ; National Natural Science Foundation of China ; National Natural Science Foundation of China |
源URL | [http://ir.iggcas.ac.cn/handle/132A11/103893] |
专题 | 中国科学院地质与地球物理研究所 |
通讯作者 | Zhao, Bo; Li, Na |
作者单位 | 1.Chinese Acad Sci, Inst Geol & Geophys, Beijing 100029, Peoples R China 2.Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai 201800, Peoples R China 3.China Special Equipment Inspect & Res Inst, Inst Chem, Beijing 10029, Peoples R China |
推荐引用方式 GB/T 7714 | Zhao, Bo,Zhao, Zhijuan,Jin, Dong,et al. The corrosion behavior and cracking susceptibility of the disbonded coating in the X80 steel pipeline by theoretical simulations and experimental measurements[J]. CORROSION REVIEWS,2021,39(6):573-587. |
APA | Zhao, Bo.,Zhao, Zhijuan.,Jin, Dong.,Li, Na.,Liu, Linlin.,...&Shou, Binan.(2021).The corrosion behavior and cracking susceptibility of the disbonded coating in the X80 steel pipeline by theoretical simulations and experimental measurements.CORROSION REVIEWS,39(6),573-587. |
MLA | Zhao, Bo,et al."The corrosion behavior and cracking susceptibility of the disbonded coating in the X80 steel pipeline by theoretical simulations and experimental measurements".CORROSION REVIEWS 39.6(2021):573-587. |
入库方式: OAI收割
来源:地质与地球物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。