Achieving superior mechanical properties of selective laser melted AlSi10Mg via direct aging treatment
文献类型：期刊论文
| 作者 | Zhang, H.1; Wang, Y.1,2; Wang, J. J.2; Ni, D. R.1; Wang, D.1; Xiao, B. L.1; Ma, Z. Y.1 |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2022-05-10 |
| 卷号 | 108页码:226-235 |
| 关键词 | Additive manufacturing Selective laser melting AlSi10Mg alloy, Heat treatment |
| ISSN号 | 1005-0302 |
| DOI | 10.1016/j.jmst.2021.07.059 |
| 通讯作者 | Ni, D. R.(drni@imr.ac.cn) ; Xiao, B. L.(blxiao@imr.ac.cn) |
| 英文摘要 | For additive manufactured aluminum alloys, the inferior mechanical properties along the building direction have been a serious weakness. In this study, an optimized heat treatment was developed as a simple and effective solution. The effects of direct aging on microstructure and mechanical properties along the building direction of AlSi10Mg samples produced via selective laser melting (SLM) were investigated. The results showed that, compared with the conventional heat treatment at elevated temperatures, direct aging at temperatures of 130-190 degrees C could retain the fine grain microstructure of SLM samples and promote further precipitation of Si phase, however, the growth of pores occurred during direct aging. With increasing aging temperature, while finer cell structures were obtained, more and larger pores were developed, resulting in decreased density of the samples. Two types of pore formation mechanisms were identified. Considering the balance between the refinement of cell structure and the growth of pores, aging at 130 degrees C was determined as the optimized heat treatment for SLM AlSi10Mg samples. The tensile strength along the building direction of the 130 degrees C aged sample was increased from 403 MPa to 451 MPa, with relatively high elongation of 6.5%. (C) 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| 资助项目 | National Key R&D Program of China[2017YFB0703104] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000787716200004 |
| 出版者 | JOURNAL MATER SCI TECHNOL |
| 资助机构 | National Key R&D Program of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/172629]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Ni, D. R.; Xiao, B. L. |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shi Changxu Innovat Ctr Adv Mat, 72 Wenhua Rd, Shenyang 110016, Peoples R China 2.Shenyang Aerosp Univ, Coll Mat Sci & Engn, 37 Daoyi South Ave, Shenyang 110136, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, H.,Wang, Y.,Wang, J. J.,et al. Achieving superior mechanical properties of selective laser melted AlSi10Mg via direct aging treatment[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2022,108:226-235. |
| APA | Zhang, H..,Wang, Y..,Wang, J. J..,Ni, D. R..,Wang, D..,...&Ma, Z. Y..(2022).Achieving superior mechanical properties of selective laser melted AlSi10Mg via direct aging treatment.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,108,226-235. |
| MLA | Zhang, H.,et al."Achieving superior mechanical properties of selective laser melted AlSi10Mg via direct aging treatment".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 108(2022):226-235. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。