Effect of rolling reduction on microstructure, texture and magnetic properties of twin-roll casting non-oriented 6.5 wt% Si electrical steel
文献类型:期刊论文
作者 | Li, Haoze |
刊名 | JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS |
出版日期 | 2022-03-15 |
卷号 | 546页码:16 |
ISSN号 | 0304-8853 |
关键词 | Non -oriented 6 5 wt% Si electrical steel Twin-roll casting Microstructure Texture Magnetic property |
DOI | 10.1016/j.jmmm.2021.168897 |
通讯作者 | Li, Haoze(lihz@imr.ac.cn) |
英文摘要 | In this study, an as-cast strip of non-oriented 6.5 wt% Si electrical steel with an equiaxed structure was fabricated by twin-roll strip casting and then treated by hot and warm rolling with different reductions, and annealing. The results showed that the as-cast microstructure was gradually pancaked and then underwent dynamic and static recrystallization as the hot rolling reduction exceeded 52%. The subsequent warm rolling brought about shear bands in part of the deformed grains. The texture evolution in the multiple rolling routes basically conformed to the classical gain-orientation rotating paths. The {00 1}-{1 1 8} (110), {223} (110) and {111} (110) texture components were intensified after warm rolling. A decreased hot rolling reduction accompanied by an increased warm rolling reduction raised the number of shear bands in the warm rolled sheets and decreased the annealing grain size. An improper combination of hot and warm rolling reductions tended to make the gamma nuclei gain the superiority in number through grain-boundary or shear-band nucleation, leading to the prevalence of the gamma annealing texture. By comparison, an alternative rolling regime adopting moderate hot (-50%) and warm rolling (-70%) reductions promoted the oriented nucleation of lambda, {1 1 4} (481) and many other non-gamma nuclei in shear bands of the {223} (110) deformed grains which had already acquired a high volume fraction in the warm rolled sheet. Consequently, mixed lambda, alpha* and gamma annealing textures were formed, giving rise to enhanced magnetic properties. The combined oriented nucleation and oriented growth mechanism was responsible for the overall evolutions of the annealing textures. |
资助项目 | National Natural Science Foundation of China[51801221] |
WOS研究方向 | Materials Science ; Physics |
语种 | 英语 |
出版者 | ELSEVIER |
WOS记录号 | WOS:000777266100001 |
资助机构 | National Natural Science Foundation of China |
源URL | [http://ir.imr.ac.cn/handle/321006/172845] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Li, Haoze |
作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Haoze. Effect of rolling reduction on microstructure, texture and magnetic properties of twin-roll casting non-oriented 6.5 wt% Si electrical steel[J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS,2022,546:16. |
APA | Li, Haoze.(2022).Effect of rolling reduction on microstructure, texture and magnetic properties of twin-roll casting non-oriented 6.5 wt% Si electrical steel.JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS,546,16. |
MLA | Li, Haoze."Effect of rolling reduction on microstructure, texture and magnetic properties of twin-roll casting non-oriented 6.5 wt% Si electrical steel".JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS 546(2022):16. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。