Effect of Zr on solidification and microstructure of a Ni-based superalloy with high Al and Ti contents
文献类型：期刊论文
| 作者 | Zhao, Guang-di2; Zang, Xi-min2; Liu, Fang1; Zhang, Wei-wei1; Gao, Shuo2; Li, Xue2; Guo, Jing2 |
| 刊名 | CHINA FOUNDRY
 |
| 出版日期 | 2022-02-01 |
| 页码 | 10 |
| 关键词 | zirconium Ni-based superalloy solidification behavior segregation TG132 3(+)3 A |
| ISSN号 | 1672-6421 |
| DOI | 10.1007/s41230-022-1058-6 |
| 通讯作者 | Zhao, Guang-di(gdzhao12s@alum.imr.ac.cn) |
| 英文摘要 | The total content of Al and Ti in advanced Ni-based wrought superalloys is up to 7.5wt.%, which makes it easier to form harmful nonequilibrium eutectic (gamma+gamma ') and eta phase. It has been reported that the addition of certain amount of Zr can modify precipitation of the nonequilibrium phases obviously, but the mechanism is still controversial. The effect of Zr ranging from <0.0006wt.% to 0.150wt.% on solidification behavior, segregation and microstructure of a Ni-based superalloy with high Al and Ti contents was investigated, eliminating the interferences of C and B. Results show that increase in Zr content significantly promotes the formation of eutectic (gamma+gamma '), eta and Zr-rich phase in the interdendritic region. Besides the Zr-rich phase, Zr dissolves slightly in the eutectic gamma ' and obviously in the eta phase. An interesting phenomenon is discovered that the Zr addition significantly increases the area fraction of liquid pools and enlarges the forming range of gamma dendrites, which suggests that Zr markedly retards the solidification. Zr affects the eutectic (gamma+gamma ') and eta formation mainly due to the retard of solidification and dissolution of Zr in them. The retard of solidification obviously increases the residual liquid fraction and undercooling. Zr can serve as a forming element for the eutectic (gamma+gamma ') and eta phase, and the obvious dissolution of Zr in eta phase significantly decreases the critical concentration of Ti for its precipitation. |
| 资助项目 | National Natural Science Foundation of China[51904146] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000750331700001 |
| 出版者 | SPRINGER SINGAPORE PTE LTD |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/173531]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhao, Guang-di |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol Liaoning, Sch Mat & Met, Anshan 114051, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhao, Guang-di,Zang, Xi-min,Liu, Fang,et al. Effect of Zr on solidification and microstructure of a Ni-based superalloy with high Al and Ti contents[J]. CHINA FOUNDRY,2022:10. |
| APA | Zhao, Guang-di.,Zang, Xi-min.,Liu, Fang.,Zhang, Wei-wei.,Gao, Shuo.,...&Guo, Jing.(2022).Effect of Zr on solidification and microstructure of a Ni-based superalloy with high Al and Ti contents.CHINA FOUNDRY,10. |
| MLA | Zhao, Guang-di,et al."Effect of Zr on solidification and microstructure of a Ni-based superalloy with high Al and Ti contents".CHINA FOUNDRY (2022):10. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。