The effect of high temperature aging on the corrosion resistance, mechanical property and antibacterial activity of Cu-2205 DSS
文献类型：期刊论文
| 作者 | Khan, M. Saleem2; Yang, Chunguang1; Pan, Haobo2; Yang, Ke1; Zhao, Ying2 |
| 刊名 | COLLOIDS AND SURFACES B-BIOINTERFACES
 |
| 出版日期 | 2022-03-01 |
| 卷号 | 211页码:9 |
| ISSN号 | 0927-7765 |
| 关键词 | Cu-2205 DSS Aging Marine environment Antimicrobial and mechanical properties Corrosion resistance |
| DOI | 10.1016/j.colsurfb.2021.112309 |
| 通讯作者 | Yang, Ke(Kyang@imr.ac.cn) ; Zhao, Ying(ying.zhao@siat.ac.cn) |
| 英文摘要 | The effects of high temperature aging on the corrosion resistance, mechanical property and antibacterial activity of a copper-bearing 2205 duplex stainless steel (Cu-2205 DSS) were investigated. The results from scanning electron microscopy (SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM) and EDS analysis showed that after aging the proportion of gamma phase in microstructure was increased and new sigma phase and copperrich precipitates were formed. The mechanical properties including hardness and tensile and yield strengths of the aged Cu-2205 DSS were significantly enhanced compared to the solution-treated Cu-2205 DSS as well as the 2205 DSS. Electrochemical measurements including electrochemical impedance spectroscopy, potentiodynamic polarization curves and potentiostatic polarization scan were performed to evaluate the corrosion behavior of the Cu-2205 DSS. It was found that aging increased the uniform corrosion resistance but had slightly adverse effect on the pitting corrosion resistance. Additionally, the antibacterial performance of aged Cu-2205 DSS was significantly improved compared to the solution treated Cu-2205 DSS, which was attributed to the more release of copper ions from the matrix that killed the bacteria cells and inhibited the biofilm formation on the surface. The above results suggest that Cu-2205 DSS after high temperature aging revealed good mechanical property, antibacterial performance, and corrosion resistance, which will further expand the application of duplex stainless steel in marine engineering fields. |
| 资助项目 | National Natural Science Foundation of China[81572113] ; National Natural Science Foundation of China[U1906226] ; National Natural Science Foundation of China[51901242] ; Science and Technology Innovation Commission of Shenzhen[JCYJ20210324102013036] |
| WOS研究方向 | Biophysics ; Chemistry ; Materials Science |
| 语种 | 英语 |
| 出版者 | ELSEVIER |
| WOS记录号 | WOS:000740205400001 |
| 资助机构 | National Natural Science Foundation of China ; Science and Technology Innovation Commission of Shenzhen |
| 源URL | [http://ir.imr.ac.cn/handle/321006/173856]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Yang, Ke; Zhao, Ying |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Shenzhen Inst Adv Technol, Shenzhen 518000, Peoples R China |
| 推荐引用方式 GB/T 7714 | Khan, M. Saleem,Yang, Chunguang,Pan, Haobo,et al. The effect of high temperature aging on the corrosion resistance, mechanical property and antibacterial activity of Cu-2205 DSS[J]. COLLOIDS AND SURFACES B-BIOINTERFACES,2022,211:9. |
| APA | Khan, M. Saleem,Yang, Chunguang,Pan, Haobo,Yang, Ke,&Zhao, Ying.(2022).The effect of high temperature aging on the corrosion resistance, mechanical property and antibacterial activity of Cu-2205 DSS.COLLOIDS AND SURFACES B-BIOINTERFACES,211,9. |
| MLA | Khan, M. Saleem,et al."The effect of high temperature aging on the corrosion resistance, mechanical property and antibacterial activity of Cu-2205 DSS".COLLOIDS AND SURFACES B-BIOINTERFACES 211(2022):9. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。