The high-cycle fatigue fracture mechanism and fatigue strength prediction of compacted graphite iron
文献类型：期刊论文
| 作者 | Zou, C. L.3; Pang, J. C.3; Qiu, Y.3; Liu, R.3; Li, S. X.3; Jing, G. X.1,2; Xu, C. G.2; Zhang, Z. F.3 |
| 刊名 | INTERNATIONAL JOURNAL OF FATIGUE
 |
| 出版日期 | 2022-08-01 |
| 卷号 | 161页码:9 |
| ISSN号 | 0142-1123 |
| 关键词 | Compacted graphite iron Microstructure High-cycle fatigue Fracture mechanism Fatigue strength prediction |
| DOI | 10.1016/j.ijfatigue.2022.106881 |
| 通讯作者 | Pang, J. C.(jcpang@imr.ac.cn) ; Zhang, Z. F.(zhfzhang@imr.ac.cn) |
| 英文摘要 | The tensile properties, high-cycle fatigue (HCF) properties and corresponding fatigue fracture mechanism of compacted graphite iron (CGI) were investigated. It is found that the tensile strength, yield strength and fatigue strength of CGI decrease as the temperature increases. At 25 ?, the fatigue cracks of CGI are mainly caused by local cleavage fracture at ferrite around the tip of vermicular graphite. At 400 ?& nbsp;and 500 ?, the gradual occurrence of grain boundary softening and oxidation may reduce the difficulty of fatigue crack propagation. Similar to temperature, the change of microstructure content also has a significant effect on the fatigue properties of CGI. By analyzing the damage characteristics of fatigue fracture morphology, it is shown that the fatigue crack initiation of CGI is mainly dependent on the damage localization caused by the ferrite and vermicular graphite inside the graphite cluster and the pearlite and spheroidal graphite outside the graphite cluster under cyclic loading. Based on those results, a fatigue strength prediction model associated with tensile strength, yield strength and microstructure area percentage was proposed. This model can provide a reasonable prediction of HCF strength of CGI at different temperatures. |
| 资助项目 | National Natural Science Foundation of China (NSFC)[51871224] ; LiaoNing Revitalization Talents Program[XLYC1808027] |
| WOS研究方向 | Engineering ; Materials Science |
| 语种 | 英语 |
| 出版者 | ELSEVIER SCI LTD |
| WOS记录号 | WOS:000793126100001 |
| 资助机构 | National Natural Science Foundation of China (NSFC) ; LiaoNing Revitalization Talents Program |
| 源URL | [http://ir.imr.ac.cn/handle/321006/173896]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Pang, J. C.; Zhang, Z. F. |
| 作者单位 | 1.Hebei Univ Technol, Tianjin Key Lab Power Transmiss & Safety Technol, Xiping Rd 5340, Tianjin 300401, Peoples R China 2.China North Engine Res Inst, 96 Yongjin Rd, Tianjin 300400, Peoples R China 3.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, 72 Wenhua Rd, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 |
Zou, C. L.,Pang, J. C.,Qiu, Y.,et al. The high-cycle fatigue fracture mechanism and fatigue strength prediction of compacted graphite iron [J]. INTERNATIONAL JOURNAL OF FATIGUE,2022,161:9. |
| APA |
Zou, C. L..,Pang, J. C..,Qiu, Y..,Liu, R..,Li, S. X..,...&Zhang, Z. F..(2022). The high-cycle fatigue fracture mechanism and fatigue strength prediction of compacted graphite iron .INTERNATIONAL JOURNAL OF FATIGUE,161,9. |
| MLA |
Zou, C. L.,et al." The high-cycle fatigue fracture mechanism and fatigue strength prediction of compacted graphite iron ".INTERNATIONAL JOURNAL OF FATIGUE 161(2022):9. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。