Effect of annealing temperature on the texture evolution and ovality of GH4145 alloy tubes with various numbers of rolling passes
文献类型:期刊论文
作者 | Wang, Leiwen2,3; Zhang, Weihong3; Zhang, Anwen1; Li, Shaowei2,3; Liu, Yingjie2,3; Sun, Wenru3 |
刊名 | JOURNAL OF ALLOYS AND COMPOUNDS |
出版日期 | 2022-07-25 |
卷号 | 910页码:9 |
ISSN号 | 0925-8388 |
关键词 | GH4145 alloy tube Ovality Texture Annealing Cold rolling |
DOI | 10.1016/j.jallcom.2022.164874 |
通讯作者 | Zhang, Weihong(whzhang@imr.ac.cn) ; Sun, Wenru(wrsun@imr.ac.cn) |
英文摘要 | The ovality variation and texture evolution with annealing temperature of GH4145 alloy tubes that were cold rolled through 2 passes, 3 passes, and 6 passes (from empty set 32 mm x 3 mm to empty set 26 mm x 1 mm) were studied. The mechanism of ovality variation was determined by laser scanning confocal microscopy, elec-tron backscattered diffraction, and X-ray diffraction. The best rolling process for GH4145 alloy tubes was identified: cold rolling through 3 passes, which resulted in an area reduction of approximately 24% per pass, followed by annealing at 920 degrees C for 30 min, via which the lowest ovality could be obtained. In terms of texture evolution, mainly S, copper, and brass textures were distributed in all cold-rolled tubes, and Goss texture was only observed in 2-pass tubes. With increasing annealing temperature, the texture strength first decreased and then increased, and the type of recrystallization texture was the same as that of cold-rolling texture, which was dominated by oriented nucleation. The higher residual stress in the cold rolling process resulted in higher ovality of the tube due to the higher energy storage. The release of residual stress during heat treatment reduced the ovality, while the enhancement of recrystallization texture led to a slight in-crease in ovality.(c) 2022 Elsevier B.V. All rights reserved. |
WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE SA |
WOS记录号 | WOS:000795084600001 |
源URL | [http://ir.imr.ac.cn/handle/321006/173941] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Zhang, Weihong; Sun, Wenru |
作者单位 | 1.Xian Thermal Power Res Inst Co Ltd, Xi'an 710054, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, 96 Jinzhai Rd, Hefei 230026, Anhui, Peoples R China 3.Chinese Acad Sci, Inst Met Res, 72 Wenhua Rd, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Leiwen,Zhang, Weihong,Zhang, Anwen,et al. Effect of annealing temperature on the texture evolution and ovality of GH4145 alloy tubes with various numbers of rolling passes[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2022,910:9. |
APA | Wang, Leiwen,Zhang, Weihong,Zhang, Anwen,Li, Shaowei,Liu, Yingjie,&Sun, Wenru.(2022).Effect of annealing temperature on the texture evolution and ovality of GH4145 alloy tubes with various numbers of rolling passes.JOURNAL OF ALLOYS AND COMPOUNDS,910,9. |
MLA | Wang, Leiwen,et al."Effect of annealing temperature on the texture evolution and ovality of GH4145 alloy tubes with various numbers of rolling passes".JOURNAL OF ALLOYS AND COMPOUNDS 910(2022):9. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。