Fabrication of ultrafine-grained Ti-15Zr-x Cu alloys through martensite decompositions under thermomechanical coupling conditions
文献类型：期刊论文
| 作者 | Gao, Wenwei2,3; Wang, Hai3; Koenigsmann, Konrad1; Zhang, Shuyuan3; Ren, Ling3; Yang, Ke3 |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2022-11-10 |
| 卷号 | 127页码:19-28 |
| ISSN号 | 1005-0302 |
| 关键词 | Titanium alloy Dynamic recrystallization Hot deformation Nucleation |
| DOI | 10.1016/j.jmst.2022.02.044 |
| 通讯作者 | Ren, Ling(lren@imr.ac.cn) |
| 英文摘要 | Grain refinement is a well-recognized method to simultaneously increase the strength and ductility of metallic materials. Fabrication of ultrafine-grained metals in bulk using a simple low-cost approach is a long-term goal for material scientists. In this work, based on the chemical composition of a biomedical Ti-15Zr alloy, a series of novel Ti-15Zr- x Cu ( x = 0, 3, 5, 7 wt.%) alloys were designed and fabricated. The alloys were quenched in the single ???phase region to obtain a martensitic microstructure and deformed in the temperature range of 710???750 ??C to obtain an ultrafine-grained microstructure through martensite decomposition under thermomechanical coupling conditions. Experimental results showed that Cu alloying could increase the dynamic recrystallization (DRX) nucleation rate due to its role in both refining martensitic lath width and increasing dislocation density. Cu alloying could also suppress grain growth due to the precipitated Ti 2 Cu particles exerting pinning forces on the grain boundaries. The optimal Cu content in the Ti-15Zr- x Cu alloy was determined to be 5 wt.%. After being subjected to a compression leading to a 70% height reduction at 730 ??C and 1 s ???1 , the grain size of the Ti-15Zr-5Cu alloy was only 180 ?? 70 nm. The tensile strength of the as-prepared alloy reached 975 ?? 10 MPa, which was 45% higher than that of the conventional Ti-15Zr alloy (673 ?? 16 MPa). This increase in strength was achieved without any reduction in ductility. The comprehensive mechanical properties of the ultrafinegrained Ti-15Zr-5Cu alloy are better than that of the Roxolid Ti???Zr alloy currently used for dental implants. ?? 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| 资助项目 | National Key Re-search and Development Program of China[2018YFC1106601] ; Doctoral Scientific Research Foundation of Liaoning Province[2020BS002] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | JOURNAL MATER SCI TECHNOL |
| WOS记录号 | WOS:000798055400002 |
| 资助机构 | National Key Re-search and Development Program of China ; Doctoral Scientific Research Foundation of Liaoning Province |
| 源URL | [http://ir.imr.ac.cn/handle/321006/174134]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Ren, Ling |
| 作者单位 | 1.Univ Chicago, Chicago, IL 60637 USA 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Gao, Wenwei,Wang, Hai,Koenigsmann, Konrad,et al. Fabrication of ultrafine-grained Ti-15Zr-x Cu alloys through martensite decompositions under thermomechanical coupling conditions[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2022,127:19-28. |
| APA | Gao, Wenwei,Wang, Hai,Koenigsmann, Konrad,Zhang, Shuyuan,Ren, Ling,&Yang, Ke.(2022).Fabrication of ultrafine-grained Ti-15Zr-x Cu alloys through martensite decompositions under thermomechanical coupling conditions.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,127,19-28. |
| MLA | Gao, Wenwei,et al."Fabrication of ultrafine-grained Ti-15Zr-x Cu alloys through martensite decompositions under thermomechanical coupling conditions".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 127(2022):19-28. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。