Effects of Brazing Temperature on Microstructure and High-Temperature Strength of Joints Using a Novel Fourth-Generation Nickel-Based Single Crystal Superalloy
文献类型：期刊论文
| 作者 | Zhang, Z. P.1,2; Liu, J. D.1; Qiu, K. Q.2; Huang, Y. Y.1; Li, J. G.1; Wang, X. G.1; Liu, J. L.1; Wang, M.1; Zou, M. K.1; Zhou, Y. Z.1 |
| 刊名 | METALS AND MATERIALS INTERNATIONAL
 |
| 出版日期 | 2022-06-03 |
| 页码 | 13 |
| ISSN号 | 1598-9623 |
| 关键词 | Superalloy Vacuum brazing Co-based filler alloy Mechanical properties |
| DOI | 10.1007/s12540-022-01223-7 |
| 通讯作者 | Liu, J. D.(jdliu@imr.ac.cn) ; Qiu, K. Q.(kqqiu@sut.edu.cn) |
| 英文摘要 | A novel fourth-generation nickel-based single crystal superalloy was bonded by vacuum brazing at 1230 degrees C, 1260 degrees C and 1290 degrees C for 60 min using a new type of Co-based filler alloy. The effects of the brazing temperature on the microstructure and mechanical properties of the brazed joint were investigated. The brazed joint was mainly composed of the non-isothermal solidification zone (M3B2 type-boride, CrB boride, Ni3B boride and MC carbide), isothermal solidification zone (gamma and gamma' Phase) and base metal. With the increase of brazing temperature, the volume fraction of borides and gamma' phase in the center of the joint decreased and increased, respectively. The high-temperature tensile test results show that the tensile strength of the joints was improved with increasing brazing temperature, and the maximum tensile strength of the joint was 766 MPa after brazing at 1290 degrees C for 60 min. Fracture observation shows that the fracture modes of the joints were the same, which belongs to the typical quasi cleavage fracture. The element distribution in the joint was homogenized to a certain extent at 1290 degrees C. The segregation of Si and Ru was found, but they were still dissolved in the gamma solid solution. The experimental results help to better understand the microstructure characteristics of the novel fourth-generation nickel-based single crystal superalloy and provide guidance for further optimizing the process parameters of the brazed joint. |
| 资助项目 | National Natural Science Foundation of China[51871221] ; National Key R&D Program of China[2017YFA0700704] ; National Science and Technology Major Project[2017-VI-0002-0072] ; National Science and Technology Major Project[J2019-VI-0023-0139] ; National Science and Technology Major Project[J2019-VII-0004-0144] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | KOREAN INST METALS MATERIALS |
| WOS记录号 | WOS:000805721700004 |
| 资助机构 | National Natural Science Foundation of China ; National Key R&D Program of China ; National Science and Technology Major Project |
| 源URL | [http://ir.imr.ac.cn/handle/321006/174254]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Liu, J. D.; Qiu, K. Q. |
| 作者单位 | 1.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China 2.Shenyang Univ Technol, Sch Mat Sci & Engn, Shenyang 110870, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, Z. P.,Liu, J. D.,Qiu, K. Q.,et al. Effects of Brazing Temperature on Microstructure and High-Temperature Strength of Joints Using a Novel Fourth-Generation Nickel-Based Single Crystal Superalloy[J]. METALS AND MATERIALS INTERNATIONAL,2022:13. |
| APA | Zhang, Z. P..,Liu, J. D..,Qiu, K. Q..,Huang, Y. Y..,Li, J. G..,...&Zhou, Y. Z..(2022).Effects of Brazing Temperature on Microstructure and High-Temperature Strength of Joints Using a Novel Fourth-Generation Nickel-Based Single Crystal Superalloy.METALS AND MATERIALS INTERNATIONAL,13. |
| MLA | Zhang, Z. P.,et al."Effects of Brazing Temperature on Microstructure and High-Temperature Strength of Joints Using a Novel Fourth-Generation Nickel-Based Single Crystal Superalloy".METALS AND MATERIALS INTERNATIONAL (2022):13. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。