Effects of Cooling Rate on the Microstructure and Tensile Properties of Powder Metallurgy Ti2AlNb Alloy
文献类型：期刊论文
| 作者 | Tian, Xiaosheng2,3; Wu, Jie3; Lu, Zhengguan3; Guo, Ruipeng1; Xu, Lei3; Yang, Rui3 |
| 刊名 | JOM
 |
| 出版日期 | 2022-05-31 |
| 页码 | 9 |
| ISSN号 | 1047-4838 |
| DOI | 10.1007/s11837-022-05338-5 |
| 通讯作者 | Xu, Lei(lxu@imr.ac.cn) |
| 英文摘要 | The effect of cooling rate on the microstructure and tensile properties of powder metallurgy (PM) Ti2AlNb alloy was studied. The Ti2AlNb pre-alloyed powder was produced by electrode induction melting gas atomization (EIGA) and then fabricated by hot isostatic pressing (HIP) at 1030 degrees C with applied pressure of 130 MPa, holding for 3 h. All samples were solution treated at 980 degrees C for 2 h, cooled at different cooling rates. The results showed that, with increasing cooling rate, the tensile strength increased to a maximum value and then decreased. The multiphase structure consists of dispersive alpha(2) phase, O phase and B2 phase matrix by furnace cooling (including four different cooling rates). At these cooling rates, all alloys have excellent elongation at room temperature (RT) and 650 degrees C. Under air cooling and water cooling, only alpha(2) and B2 phase exist in these alloys, and they have better elongation at room temperature. At 650 degrees C, a sharp drop in plasticity has been obtained because of the fine acicular O phase precipitates, which will reduce the resistance of crack propagation along the prior B2 grain boundary. |
| 资助项目 | CAS Project for Young Scientists in Basic Research[YSBR-025] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering ; Mineralogy ; Mining & Mineral Processing |
| 语种 | 英语 |
| WOS记录号 | WOS:000803856200001 |
| 出版者 | SPRINGER |
| 资助机构 | CAS Project for Young Scientists in Basic Research |
| 源URL | [http://ir.imr.ac.cn/handle/321006/174308]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Xu, Lei |
| 作者单位 | 1.Taiyuan Univ Technol, Coll Mat Sci & Engn, Taiyuan 030024, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Tian, Xiaosheng,Wu, Jie,Lu, Zhengguan,et al. Effects of Cooling Rate on the Microstructure and Tensile Properties of Powder Metallurgy Ti2AlNb Alloy[J]. JOM,2022:9. |
| APA | Tian, Xiaosheng,Wu, Jie,Lu, Zhengguan,Guo, Ruipeng,Xu, Lei,&Yang, Rui.(2022).Effects of Cooling Rate on the Microstructure and Tensile Properties of Powder Metallurgy Ti2AlNb Alloy.JOM,9. |
| MLA | Tian, Xiaosheng,et al."Effects of Cooling Rate on the Microstructure and Tensile Properties of Powder Metallurgy Ti2AlNb Alloy".JOM (2022):9. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。