Corrosion performance of epoxy coatings modified by nanoparticulate SiO2
文献类型:期刊论文
作者 | Li, W.1; Tian, H.1,2; Hou, B.1 |
刊名 | MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION |
出版日期 | 2012 |
卷号 | 63期号:1页码:44-53 |
ISSN号 | 0947-5117 |
关键词 | corrosion performance epoxy coating modification nanoparticulate SiO2 |
通讯作者 | Li, W (reprint author), Chinese Acad Sci, Inst Oceanol, Key Lab Corros Sci Shandong, Qingdao 266071, Peoples R China. |
英文摘要 | Electrochemical impedance spectroscopy (EIS) was employed to investigate the corrosion performance of nanoparticulate SiO2 modified epoxy coatings on carbon steel in 3.5?wt% NaCl solution, coupled with salt spray test. Capacitance-gravimetric methods and delamination tests were performed to analyze the water uptake behavior and interface stability against delamination of modified coatings, respectively. Four systems were studied, including a clear coating and three pigmented coatings (with 1, 2, and 3?wt% nanoparticulate SiO2). The experimental results showed that nanoparticulate SiO2 particles can improve the anti-corrosion performance of the coatings and the optimal addition content is 2?wt%. The results obtained with capacitance-gravimetric measurements showed that the diffusion process of water through epoxy coatings with different pigment volume concentration (PVC) obeyed the second Fick's diffusion law in the initial period. Adding nanoparticulate SiO2 into epoxy coatings can act effectively. The positive influence is attributed to the reaction between nanoparticles and epoxy resin which is confirmed by FTIR, improving the barrier and dispersion effectiveness of coatings. The negative one is increasing the number of pores in the coatings when the adding amount is beyond the critical PVC. |
学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
收录类别 | SCI |
原文出处 | 10.1002/maco.200905620 |
语种 | 英语 |
WOS记录号 | WOS:000298919900005 |
公开日期 | 2013-09-24 |
源URL | [http://ir.qdio.ac.cn/handle/337002/12462] |
专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
作者单位 | 1.Chinese Acad Sci, Inst Oceanol, Key Lab Corros Sci Shandong, Qingdao 266071, Peoples R China 2.Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Li, W.,Tian, H.,Hou, B.. Corrosion performance of epoxy coatings modified by nanoparticulate SiO2[J]. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,2012,63(1):44-53. |
APA | Li, W.,Tian, H.,&Hou, B..(2012).Corrosion performance of epoxy coatings modified by nanoparticulate SiO2.MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,63(1),44-53. |
MLA | Li, W.,et al."Corrosion performance of epoxy coatings modified by nanoparticulate SiO2".MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION 63.1(2012):44-53. |
入库方式: OAI收割
来源:海洋研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。