Effect of the 345 degrees C and 16.5 MPa autoclave corrosion on the oxidation behavior of Cr-coated zirconium claddings in the high-temperature steam
文献类型：期刊论文
| 作者 | Liu, Haiyong; Feng, Yajie; Yao, Yirong; Li, Bingsheng; Wang, Renda; Shi, Xiaoguang; Li, Peng; Shu, Jie; Huang, Feng; Huang, Qing |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2021 |
| 卷号 | 189 |
| 关键词 | CHROMIUM HYDROGEN GROWTH |
| 英文摘要 | Cr-coated Zirlo tubes were conducted in the autoclave corrosion (345 degrees C and 16.5 MPa), followed by the 1200 degrees C steam oxidation. After the 1-h oxidation, the coated tubes exhibited structural integrity, in contrast to the uncoated ones that had broken into pieces. Moreover, the coated tubes that already underwent the 45-days precorrosion, still remained good oxidation resistance with the weight gain of -4.46 mg/cm2. During the precorrosion, very thin Cr2O3 tissue formed on the outmost surface and along the columnar boundaries, which would suppress the formation of bubbles and cracks in the subsequent oxidation. |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/21653]  |
| 专题 | 中国科学院宁波材料技术与工程研究所 2021专题_期刊论文 |
| 作者单位 | Ge, FF (corresponding author), Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Engn Lab Adv Energy Mat, Ningbo 315201, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Liu, Haiyong,Feng, Yajie,Yao, Yirong,et al. Effect of the 345 degrees C and 16.5 MPa autoclave corrosion on the oxidation behavior of Cr-coated zirconium claddings in the high-temperature steam[J]. CORROSION SCIENCE,2021,189. |
| APA | Liu, Haiyong.,Feng, Yajie.,Yao, Yirong.,Li, Bingsheng.,Wang, Renda.,...&Ge, Fangfang.(2021).Effect of the 345 degrees C and 16.5 MPa autoclave corrosion on the oxidation behavior of Cr-coated zirconium claddings in the high-temperature steam.CORROSION SCIENCE,189. |
| MLA | Liu, Haiyong,et al."Effect of the 345 degrees C and 16.5 MPa autoclave corrosion on the oxidation behavior of Cr-coated zirconium claddings in the high-temperature steam".CORROSION SCIENCE 189(2021). |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。