The outstanding effect and mechanism of non-inert casting atmospheres on glass forming ability of P-containing Fe-based soft magnetic bulk metallic glasses
文献类型：期刊论文
| 作者 | Zhang, Jianhua; Zhang, Chengzhong; Zhang, Xiaoxiong; Li, Zhien; He, Aina; Song, Jiancheng; Chang, Chuntao |
| 刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| 出版日期 | 2021 |
| 卷号 | 866 |
| 英文摘要 | Generally, amorphous alloys are fabricated in an inert atmosphere-Ar to avoid crystallization and gain high glass forming ability (GFA). In this work, the effect of non-inert casting atmospheres (N-2, air and O-2) on the GFA of Fe76Si9B10P5, Fe76Si8B10P5Mo1, Fe77Mo2P10C4B4Si3 and [(Fe0.8Co0.2)(0.75)B0.2Si0.05](96)Nb-4 soft magnetic bulk metallic glasses (BMGs) was systematically investigated. Surprisingly, contrary to existing experience, while the GFA of [(Fe0.8Co0.2)(0.75)B0.2Si0.05](96)Nb-4 alloy remains the same as cast in Ar, it was found that the non-inert casting atmospheres can dramatically improve the GFA of P-containing Fe-based BMGs, especially in oxidizing casting atmosphere, with no influence in their thermal properties and magnetic properties. The results also indicated the surface composition of the P-containing Fe-based BMGs varied much with the casting atmospheres whilst the bulk composition remain unchanged. Moreover, plausible reasons were eliminated and underlying mechanism was elucidated. The decreased surface tension resulted from the segregation of P element of the P-containing Fe-based liquids during the melting process leads to the crystallization occurring in the surface layer rather than in the central area. At last, the enhancement of GFA by non-inert casting atmospheres were mainly ascribed to the increased surface tension resulting from the elimination of oxygen element for the oxidizing (air and O-2) atmosphere and the alloying effect of nitrogen element for the N-2 atmosphere, respectively. The new understanding about the non-inert atmosphere and metallic amorphous formation is expected to benefit the composition design of amorphous materials with better GFA and advances in the manufacture of amorphous alloys. (C) 2021 Elsevier B.V. All rights reserved. |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/21832]  |
| 专题 | 中国科学院宁波材料技术与工程研究所 2021专题_期刊论文 |
| 作者单位 | Zhang, JH (corresponding author), Taiyuan Univ Technol, Coll Elect & Power Engn, Natl & Prov Joint Engn Lab Min Intelligent Elect, Shanxi Key Lab Coal Min Equipment & Safety Contro, 79 Yingze West Ave, Taiyuan 030024, Shanxi, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Zhang, Jianhua,Zhang, Chengzhong,Zhang, Xiaoxiong,et al. The outstanding effect and mechanism of non-inert casting atmospheres on glass forming ability of P-containing Fe-based soft magnetic bulk metallic glasses[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2021,866. |
| APA | Zhang, Jianhua.,Zhang, Chengzhong.,Zhang, Xiaoxiong.,Li, Zhien.,He, Aina.,...&Chang, Chuntao.(2021).The outstanding effect and mechanism of non-inert casting atmospheres on glass forming ability of P-containing Fe-based soft magnetic bulk metallic glasses.JOURNAL OF ALLOYS AND COMPOUNDS,866. |
| MLA | Zhang, Jianhua,et al."The outstanding effect and mechanism of non-inert casting atmospheres on glass forming ability of P-containing Fe-based soft magnetic bulk metallic glasses".JOURNAL OF ALLOYS AND COMPOUNDS 866(2021). |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。