An in situ TEM nanoindentation-induced new nanostructure in cadmium zinc telluride
文献类型:期刊论文
作者 | Liu, Dongdong; Zhang, Zhenyu; Chen, Leilei; Wang, Dong; Cui, Junfeng; Chang, Keke; Guo, Dongming |
刊名 | NANOSCALE |
出版日期 | 2021 |
卷号 | 13期号:15页码:7169-7175 |
关键词 | SINGLE-CRYSTALS MECHANICAL-PROPERTIES CDTE NANOCRYSTALS PEIERLS STRESSES LOW-COST SURFACE DYNAMICS |
英文摘要 | Phase transformations occurring in a solid govern the structural and physical properties significantly. Nevertheless, deformation-induced phase transition in a soft-brittle solid has not been demonstrated yet. Soft-brittle cadmium zinc telluride (CZT) based instruments have produced technological breakthroughs in the semiconductor industry, and therefore their phase transformations have been widely investigated during the past 60 years. In this study, in situ transmission electron microscopy (TEM) nanoindentation was performed on CZT, and it was found that no brittle fracture occurred at a peak load of 41.9 mu N, corresponding to a stress of 1.75 GPa. A new nanostructure induced by in situ TEM nanoindentation was observed, consisting of a single crystal, slip bands, stacking faults, a superlattice, a new tetragonal phase, and Moire fringes. The new tetragonal phase was formed by partial Cd and Te atoms in the (11 $$(1) over bar) plane slipping along the [(1) over bar2 (1) over bar] orientation, which was elucidated by ab initio simulations. It belongs to a tetragonal crystal system, and the lattice distances along the X and Y axes were 0.382 and 0.376 nm, respectively. Our findings provide new insights into the deformation-induced phase transformation for a soft-brittle solid, and have application potential in solar cells, radiation detectors, and medical imaging, quantum, flexible electronic and optoelectronic devices. |
源URL | [http://ir.nimte.ac.cn/handle/174433/22007] |
专题 | 中国科学院宁波材料技术与工程研究所 2021专题_期刊论文 |
作者单位 | Zhang, ZY (corresponding author), Dalian Univ Technol, Minist Educ, Key Lab Precis & Nontradit Machining Technol, Dalian 116024, Peoples R China. |
推荐引用方式 GB/T 7714 | Liu, Dongdong,Zhang, Zhenyu,Chen, Leilei,et al. An in situ TEM nanoindentation-induced new nanostructure in cadmium zinc telluride[J]. NANOSCALE,2021,13(15):7169-7175. |
APA | Liu, Dongdong.,Zhang, Zhenyu.,Chen, Leilei.,Wang, Dong.,Cui, Junfeng.,...&Guo, Dongming.(2021).An in situ TEM nanoindentation-induced new nanostructure in cadmium zinc telluride.NANOSCALE,13(15),7169-7175. |
MLA | Liu, Dongdong,et al."An in situ TEM nanoindentation-induced new nanostructure in cadmium zinc telluride".NANOSCALE 13.15(2021):7169-7175. |
入库方式: OAI收割
来源:宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。