Surface treatment of titanium by in-situ anodizination and NiO photodeposition: enhancement of photoelectrochemical properties for water splitting and photocathodic protection of stainless steel
文献类型:期刊论文
作者 | Sharifi, Tayebeh; Ghayeb, Yousef; Mohammadi, Tecush; Momeni, Mohamad Mohsen; Bagheri, Robabeh; Song, Zhenlun |
刊名 | APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING |
出版日期 | 2021 |
卷号 | 127期号:1 |
关键词 | TIO2 NANOTUBE ARRAYS PHOTOCATALYTIC DEGRADATION HYDROGEN GENERATION EVOLUTION NANOCOMPOSITE PHOTOANODES PERFORMANCE COMPOSITES CATALYSTS ALCOHOL |
英文摘要 | Chromium-doped TiO2 nanotubes (CT) film on titanium substrates was prepared by an in-situ electrochemical anodizing method and then a wide range time was used for photodeposition of NiO on the surface of CT to optimize the condition for the fabrication of NiO-chromium-doped TiO2 nanotubes (NCT). Various techniques were used to characterization which confirms the anatase form of TiO2 as well as the presence of NiO. The UV-Vis spectra exhibit that deposited of NiO on the surface of CT progressively enhances visible light absorption. Photoelectrochemical performance of as-prepared samples was studied in the presence and absence of light which showed that NCT samples are markedly beneficial for reducing photo generated charges recombination. NCT2 sample effectively increased photocurrent density four times more than the bare CT sample and showed the maximum amount of H-2 evolution during water splitting after 60 min. In addition, Tafel tests are performed to investigate the photocathodic protection of as-prepared samples for 403 stainless steel. It was observed that the photocathodic protection performance is achieved for NCT2 which prepared at a photodeposition time of 20 min. |
源URL | [http://ir.nimte.ac.cn/handle/174433/22336] |
专题 | 中国科学院宁波材料技术与工程研究所 2021专题_期刊论文 |
作者单位 | Ghayeb, Y (corresponding author), Isfahan Univ Technol, Dept Chem, Esfahan 8415683111, Iran. |
推荐引用方式 GB/T 7714 | Sharifi, Tayebeh,Ghayeb, Yousef,Mohammadi, Tecush,et al. Surface treatment of titanium by in-situ anodizination and NiO photodeposition: enhancement of photoelectrochemical properties for water splitting and photocathodic protection of stainless steel[J]. APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING,2021,127(1). |
APA | Sharifi, Tayebeh,Ghayeb, Yousef,Mohammadi, Tecush,Momeni, Mohamad Mohsen,Bagheri, Robabeh,&Song, Zhenlun.(2021).Surface treatment of titanium by in-situ anodizination and NiO photodeposition: enhancement of photoelectrochemical properties for water splitting and photocathodic protection of stainless steel.APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING,127(1). |
MLA | Sharifi, Tayebeh,et al."Surface treatment of titanium by in-situ anodizination and NiO photodeposition: enhancement of photoelectrochemical properties for water splitting and photocathodic protection of stainless steel".APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING 127.1(2021). |
入库方式: OAI收割
来源:宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。