Effect of surface Nd-rich phase and oxygen content of melt-spun flakes on formation of coarse grains in hot-pressed Nd-Fe-B magnet
文献类型：期刊论文
| 作者 | Du, Yeyuan; Yin, Wenzong; Chen, Renjie; Tang, Xu; Ju, Jinyun; Chen, Bin; Hou, Longquan; Yan, Aru; Yuan, Jianhui |
| 刊名 | JOURNAL OF RARE EARTHS
 |
| 出版日期 | 2021 |
| 卷号 | 39期号:11页码:1389-1395 |
| 关键词 | DEFORMED MAGNETS MICROSTRUCTURE DEFORMATION IMPROVEMENT COERCIVITY TEXTURE PR |
| 英文摘要 | Nd-Fe-B hot-pressed (HP) magnet prepared from melt-spun MQU-F flakes features coarse grains (CG) with the average size of both 200 nm (CG(S)) and 700 nm (CG(L)) at flake boundary. The grain growth at the flake boundary of Nd2Fe14B/alpha-Fe composite HP magnet before and after diffusion of low-melting-point Pr82Cu18 phase was investigated, revealing the indispensable role of surface RE-rich phase of melt-spun flakes in the formation of CG in HP magnet. The dominant role of surface oxygen content of melt-spun flakes in the formation of CG(L) has been clarified with etching method. The HP magnet prepared from the etched flakes with dramatically decreased oxygen content exhibits the CG regions merely with homogeneous equiaxed CG(S) at flake boundary. Consequently, the coercivity (mu H-0(c)) shows significant increase while remanent magnetization (mu M-0(r)) inappreciable change. Further investigation with sieving method reveals the elimination of CG(L) via removal of the fine Nd-Fe-B flakes smaller than 54 mu m due to their much higher oxygen content, confirming the dominant role of oxygen content in the formation of CG(L). The quantitative analysis on the magnetic properties of the above HP magnets reveals the monotonic increase of coercivity (mu H-0(c)) and negligible change of remanent magnetization (mu M-0(r)) with decreased oxygen contents of Nd-Fe-B flakes. The maximum value of coercivity (mu H-0(c)) increases from 2.26 to 2.47 T as the oxygen content decreases from 0.1692 wt% to 0.079 wt%. (C) 2021 The Authors. Published by Elsevier B.V. |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/21336]  |
| 专题 | 2021专题_期刊论文 |
| 作者单位 | 1.Yin, WZ 2.Chen, RJ (corresponding author), Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Key Lab Magnet Mat & Devices, Ningbo 315201, Peoples R China. 3.Yuan, JH (corresponding author), Shanghai Univ Engn Sci, Shanghai Collaborat Innovat Ctr Laser Adv Mfg Tec, Sch Mat Engn, Shanghai 201620, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Du, Yeyuan,Yin, Wenzong,Chen, Renjie,et al. Effect of surface Nd-rich phase and oxygen content of melt-spun flakes on formation of coarse grains in hot-pressed Nd-Fe-B magnet[J]. JOURNAL OF RARE EARTHS,2021,39(11):1389-1395. |
| APA | Du, Yeyuan.,Yin, Wenzong.,Chen, Renjie.,Tang, Xu.,Ju, Jinyun.,...&Yuan, Jianhui.(2021).Effect of surface Nd-rich phase and oxygen content of melt-spun flakes on formation of coarse grains in hot-pressed Nd-Fe-B magnet.JOURNAL OF RARE EARTHS,39(11),1389-1395. |
| MLA | Du, Yeyuan,et al."Effect of surface Nd-rich phase and oxygen content of melt-spun flakes on formation of coarse grains in hot-pressed Nd-Fe-B magnet".JOURNAL OF RARE EARTHS 39.11(2021):1389-1395. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。