Synergistic effects of B-In codoping in zone-melted Bi0.48Sb1.52Te3-based thermoelectric
文献类型：期刊论文
| 作者 | Wang, Hongxiang; Wu, Gang; Yan, Zipeng; Tan, Xiaojian; Cai, Jianfeng; Hu, Haoyang; Sun, Peng; Liu, Guoqiang; Jiang, Jun |
| 刊名 | CHEMICAL ENGINEERING JOURNAL
 |
| 出版日期 | 2021 |
| 卷号 | 420 |
| 关键词 | P-TYPE BI0.48SB1.52TE3 THERMAL-CONDUCTIVITY PERFORMANCE FIGURE MERIT POWER ALLOY BISBTE HEAT |
| 英文摘要 | Bismuth-telluride-based alloys are the unique commercial thermoelectric materials near room temperature, and the commonly used zone-melting method is efficient for the mass production. Since the ZTs of zone-melted samples has stagnated around 1.2 for decades, it is urgent for the scientific and industrial societies to break through this bottleneck. Herein, we report simultaneously improved power factor and ZT values in p-type Bi0.48Sb1.52Te3 materials by the addition of amorphous boron and metal indium. B and In dopants not only effectively increase the hole concentration and the density of state effective mass, leading to a high power factor of 55 mu W cm-1 K-2, but also introduce various phonon scattering centers to obviously suppress the lattice thermal conductivity. The synergistic effects yield a ZTmax of 1.45 at 350 K, as well as a ZTave of 1.20 and sigma S2ave of 41 mu W cm-1 K-2 (300 - 500 K) in the Bi0.48Sb1.515In0.005Te3 + 0.6 wt% B sample, suggesting tiny B-In codoping is a promising strategy for the further development of bismuth telluride thermoelectrics. |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/21502]  |
| 专题 | 2021专题_期刊论文 |
| 作者单位 | Tan, XJ (corresponding author), Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Ningbo 315201, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Wang, Hongxiang,Wu, Gang,Yan, Zipeng,et al. Synergistic effects of B-In codoping in zone-melted Bi0.48Sb1.52Te3-based thermoelectric[J]. CHEMICAL ENGINEERING JOURNAL,2021,420. |
| APA | Wang, Hongxiang.,Wu, Gang.,Yan, Zipeng.,Tan, Xiaojian.,Cai, Jianfeng.,...&Jiang, Jun.(2021).Synergistic effects of B-In codoping in zone-melted Bi0.48Sb1.52Te3-based thermoelectric.CHEMICAL ENGINEERING JOURNAL,420. |
| MLA | Wang, Hongxiang,et al."Synergistic effects of B-In codoping in zone-melted Bi0.48Sb1.52Te3-based thermoelectric".CHEMICAL ENGINEERING JOURNAL 420(2021). |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。