Cr/GLC multilayered coating in simulated deep-sea environment: Corrosion behavior and growth defect evolution
文献类型：期刊论文
| 作者 | Liu, Yingrui; Du, Hong; Zuo, Xiao; Guo, Peng; Liu, Li; Lee, Kwang-Ryeol; Wang, Aiying; Ke, Peiling |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2021 |
| 卷号 | 188 |
| 关键词 | ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY NACL AQUEOUS-SOLUTION PVD COATED STEELS HYDROSTATIC-PRESSURE FAILURE BEHAVIOR CR FILMS EIS RESISTANCE METALS |
| 英文摘要 | In this work, the corrosion behavior of the multilayered Cr/GLC coating was evaluated in artificial seawater by comparison at an atmospheric pressure (1 atm) and a higher hydrostatic pressure (300 atm). The results revealed that the corrosion resistance of the coating was more favorable at 1 atm, but the hydrostatic pressure deteriorated coating protectiveness significantly by rapidly accelerating seawater diffusion through the growth defect and promoting the exposure of the substrate. The localized corrosion induced by the penetrating defect became more susceptible. This study is helpful to bring forward the significant guideline to fabricate the dense coating for deep-sea applications. |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/21601]  |
| 专题 | 2021专题_期刊论文 |
| 作者单位 | Ke, PL (corresponding author), Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Key Lab Marine Mat & Related Technol, Zhejiang Key Lab Marine Mat & Protect Technol, Ningbo 315201, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Liu, Yingrui,Du, Hong,Zuo, Xiao,et al. Cr/GLC multilayered coating in simulated deep-sea environment: Corrosion behavior and growth defect evolution[J]. CORROSION SCIENCE,2021,188. |
| APA | Liu, Yingrui.,Du, Hong.,Zuo, Xiao.,Guo, Peng.,Liu, Li.,...&Ke, Peiling.(2021).Cr/GLC multilayered coating in simulated deep-sea environment: Corrosion behavior and growth defect evolution.CORROSION SCIENCE,188. |
| MLA | Liu, Yingrui,et al."Cr/GLC multilayered coating in simulated deep-sea environment: Corrosion behavior and growth defect evolution".CORROSION SCIENCE 188(2021). |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。