Thermal shock behaviour and failure mechanism of two-kind Cr coatings on non-planar structure
文献类型：期刊论文
| 作者 | Hu, Ming1,3,4; Pan, Mengfei4; Shen, Mingli2; Guo, Cean4; Tang, Yueyang4; Yu, Hangjian4 |
| 刊名 | ENGINEERING FAILURE ANALYSIS
 |
| 出版日期 | 2022-11-01 |
| 卷号 | 141页码:12 |
| ISSN号 | 1350-6307 |
| 关键词 | Thermal shock behaviour Cr coating Non-planar structure Electroplating Vacuum arc ion plating |
| DOI | 10.1016/j.engfailanal.2022.106697 |
| 通讯作者 | Hu, Ming(minghu_sylu@163.com) |
| 英文摘要 | Cr coating is widely used as a protective coating on the inner and outer surface of industrial equipment. However, current researches on Cr coatings are predominantly conducted on plane specimens, and few works have considered the effect of irregular substrates on coatings. The thermal shock behaviour and failure mechanisms of two-kind Cr coatings prepared by electro-plating and vacuum arc ion plating on non-planar structure at 900 C were investigated. The microstructure and crystalline phases of the two-kind Cr coatings were analysed by scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction. The results indicate that vacuum arc ion plating Cr coating has better thermal shock resistance. There were two typical damaged regions for both Cr coatings, i.e.the concave corner of groove and the convex corner of land. By analysing the thermal shock damage behaviour of the coatings, it is concluded that fatigue stress, thermal mismatch stress, and the inherent properties of the two-kind Cr coatings are the main reasons for the difference in the overall damage degree, and the temper-ature stress concentration in the concave corner of groove is the cause for the higher degree of thermal shock damage. |
| 资助项目 | Department of Science and Technology of Liaoning Province[2021 -BS -162] ; Basic Research Project for Higher Education Institutions of the Education Department of Liaoning Province[LJKZ0273] |
| WOS研究方向 | Engineering ; Materials Science |
| 语种 | 英语 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| WOS记录号 | WOS:000848499100002 |
| 资助机构 | Department of Science and Technology of Liaoning Province ; Basic Research Project for Higher Education Institutions of the Education Department of Liaoning Province |
| 源URL | [http://ir.imr.ac.cn/handle/321006/175028]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Hu, Ming |
| 作者单位 | 1.Shenyang Ligong Univ, 6 Nanpingzhong Rd, Shenyang 110159, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang, Peoples R China 3.Inner Mongolia North Heavy Ind Grp Co, Baotou, Peoples R China 4.Shenyang Ligong Univ, Sch Equipment Engn, Shenyang, Peoples R China |
| 推荐引用方式 GB/T 7714 | Hu, Ming,Pan, Mengfei,Shen, Mingli,et al. Thermal shock behaviour and failure mechanism of two-kind Cr coatings on non-planar structure[J]. ENGINEERING FAILURE ANALYSIS,2022,141:12. |
| APA | Hu, Ming,Pan, Mengfei,Shen, Mingli,Guo, Cean,Tang, Yueyang,&Yu, Hangjian.(2022).Thermal shock behaviour and failure mechanism of two-kind Cr coatings on non-planar structure.ENGINEERING FAILURE ANALYSIS,141,12. |
| MLA | Hu, Ming,et al."Thermal shock behaviour and failure mechanism of two-kind Cr coatings on non-planar structure".ENGINEERING FAILURE ANALYSIS 141(2022):12. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。