Honeycomb structure with oxygen-poor pores at the top of magnetite layer on a martensitic steel CLAM exposed to lead-bismuth eutectic at 500 ºC
文献类型:期刊论文
作者 | Lin Luo1,2; Zunqi Xiao2; Min Zhang2; Zhizhong Jiang1,2; Jing Liu2; Wangli Huang2; Lujun Sun2 |
刊名 | Corrosion Science |
出版日期 | 2022-05-30 |
DOI | 10.1016/j.corsci.2022.110410 |
源URL | [http://ir.hfcas.ac.cn:8080/handle/334002/132336] |
专题 | 合肥物质科学研究院_中国科学院核能安全技术研究所 |
通讯作者 | Zhizhong Jiang; Jing Liu |
作者单位 | 1.University of Science and Technology of China, Hefei 230026, China 2.Institute of Nuclear Energy Safety Technology, Hefei Institutes of Physical Science, Chinese Academy of Sciences, Hefei 230031, China |
推荐引用方式 GB/T 7714 | Lin Luo,Zunqi Xiao,Min Zhang,et al. Honeycomb structure with oxygen-poor pores at the top of magnetite layer on a martensitic steel CLAM exposed to lead-bismuth eutectic at 500 ºC[J]. Corrosion Science,2022. |
APA | Lin Luo.,Zunqi Xiao.,Min Zhang.,Zhizhong Jiang.,Jing Liu.,...&Lujun Sun.(2022).Honeycomb structure with oxygen-poor pores at the top of magnetite layer on a martensitic steel CLAM exposed to lead-bismuth eutectic at 500 ºC.Corrosion Science. |
MLA | Lin Luo,et al."Honeycomb structure with oxygen-poor pores at the top of magnetite layer on a martensitic steel CLAM exposed to lead-bismuth eutectic at 500 ºC".Corrosion Science (2022). |