Anti-Corrosion Performance of Migratory Corrosion Inhibitors on Reinforced Concrete Exposed to Varying Degrees of Chloride Erosion

文献类型：期刊论文

作者Sun, Congtao1,2; Sun, Ming1,2; Liu, Junde3; Dong, Zhenping3; Fan, Liang1,2; Duan, Jizhou1,2
刊名MATERIALS
出版日期2022-08-01
卷号15期号:15页码:12
关键词anti-corrosion performance MCIs reinforced concrete chloride erosion steel bar
DOI10.3390/ma15155138
通讯作者Sun, Congtao(suncongtao@qdio.ac.cn) ; Dong, Zhenping(dongzp_02@163.com)
英文摘要This study investigated the anti-corrosion performance of commercial amino alcohol migratory corrosion inhibitors (MCIs) on concrete that underwent varying degrees of chloride erosion. Electrochemical impedance spectroscopy (EIS), potentiodynamic polarization (PD), scanning electron microscopy, and energy dispersive spectroscopy (SEM-EDS) analyses were performed to study the anti-corrosion performance and mechanism of the MCIs on the steel bars. The results indicated that the corrosion resistance of the steel bars in concrete was significantly improved by coating with the MCIs, and the earlier the specimens were coated with the MCIs, the higher the anti-corrosion efficiency. The anti-corrosion efficiency was 55.35% when the MCIs coating was applied before chloride erosion; however, the anti-corrosion efficiency decreased to 3.40% when the MCIs coating was applied after the ninth drying-wetting cycle. The improvement in corrosion resistance of the steel bar in concrete coated with MCIs was due to the protective MCIs-molecule film that formed on the steel bar surfaces, and the oxidative dissolution of iron at the anode was effectively inhibited by the MCIs coating.
资助项目National Natural Science Foundation of China[41827805] ; Natural Science Key Foundation of Shandong Province[ZR2020KE046] ; Strategic Priority Project of CAS[XDA13040402]
WOS研究方向Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering ; Physics
语种英语
WOS记录号WOS:000839206100001
出版者MDPI
源URL[http://ir.qdio.ac.cn/handle/337002/179937]  
专题海洋研究所_海洋腐蚀与防护研究发展中心
通讯作者Sun, Congtao; Dong, Zhenping
作者单位1.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China
2.Pilot Natl Lab Marine Sci & Technol Qingdao, Open Studio Marine Corros & Protect, Qingdao 266237, Peoples R China
3.Xian Univ Architecture & Technol, Sch Civil Engn, Xian 710055, Peoples R China
推荐引用方式
GB/T 7714		 Sun, Congtao,Sun, Ming,Liu, Junde,et al. Anti-Corrosion Performance of Migratory Corrosion Inhibitors on Reinforced Concrete Exposed to Varying Degrees of Chloride Erosion[J]. MATERIALS,2022,15(15):12.
APA Sun, Congtao,Sun, Ming,Liu, Junde,Dong, Zhenping,Fan, Liang,&Duan, Jizhou.(2022).Anti-Corrosion Performance of Migratory Corrosion Inhibitors on Reinforced Concrete Exposed to Varying Degrees of Chloride Erosion.MATERIALS,15(15),12.
MLA Sun, Congtao,et al."Anti-Corrosion Performance of Migratory Corrosion Inhibitors on Reinforced Concrete Exposed to Varying Degrees of Chloride Erosion".MATERIALS 15.15(2022):12.

入库方式： OAI收割

来源：海洋研究所

浏览0
下载0
收藏0
其他版本

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。