Mesoporous LaCoO3 perovskite oxide with high catalytic performance for NOx storage and reduction
文献类型：期刊论文
| 作者 | Xie, Wen; Xu, Guangyan; Zhang, Yan ; Yu, Yunbo; He, Hong
|
| 刊名 | JOURNAL OF HAZARDOUS MATERIALS
 |
| 出版日期 | 2022-06-05 |
| 卷号 | 431期号:0页码:128528 |
| 关键词 | LEAN/RICH ATMOSPHERES SURFACE-AREA ACTIVE-SITES OXIDATION REGENERATION PARTICLES TOLERANCE REMOVAL TOLUENE SILICA |
| ISSN号 | 0304-3894 |
| 英文摘要 | A mesoporous LaCoO3 perovskite oxide (LaCoO3-Meso) with three-dimensionally ordered helical interwoven structure was synthesized by a nano-casting method using KIT-6 as the hard template. The obtained LaCoO3-Meso with high surface area was tested for its catalytic performance in the NOx storage and reduction (NSR) reaction and compared with a sample synthesized by the conventional sol-gel method. The LaCoO3-Meso showed a significant advantage for NOx storage, with a NOx storage capacity 2 times higher than the regular sample. LaCoO3-Meso also exhibited improved NSR catalytic performance in the 150-450 degrees C temperature range, especially within 350-400 degrees C, where the NOx conversion was raised for 40%. The results of X-ray photoelectron spectroscopy and X-ray absorption fine structure measurements suggested the presence of a high concentration of oxygen defects on the LaCoO3-Meso surface. Further results provided by temperature programmed reduction and temperature programmed desorption indicated that the oxygen defects not only increase the amount of trapped NOx , but also improve the low-temperature redox performance of the catalyst. The lower stability of NOx species adsorbed on oxygen defects promotes the NOx release step in the NSR reaction and benefits the regeneration of storage sites. |
| 源URL | [https://ir.rcees.ac.cn/handle/311016/47420]  |
| 专题 | 生态环境研究中心_大气污染控制中心 |
| 作者单位 | 1.Chinese Acad Sci, Ctr Excellence Reg Atmospher Environm, Inst Urban Environm, Xiamen 361021, Peoples R China 2.Chinese Acad Sci, Res Ctr Ecoenvironm Sci, State Key Joint Lab Environm Simulat & Pollut Con, Beijing 100085, Peoples R China 3.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 4.Chinese Acad Sci, Ganjiang Innovat Acad, Ganzhou 341000, Peoples R China |
| 推荐引用方式 GB/T 7714 | Xie, Wen,Xu, Guangyan,Zhang, Yan,et al. Mesoporous LaCoO3 perovskite oxide with high catalytic performance for NOx storage and reduction[J]. JOURNAL OF HAZARDOUS MATERIALS,2022,431(0):128528. |
| APA | Xie, Wen,Xu, Guangyan,Zhang, Yan,Yu, Yunbo,&He, Hong.(2022).Mesoporous LaCoO3 perovskite oxide with high catalytic performance for NOx storage and reduction.JOURNAL OF HAZARDOUS MATERIALS,431(0),128528. |
| MLA | Xie, Wen,et al."Mesoporous LaCoO3 perovskite oxide with high catalytic performance for NOx storage and reduction".JOURNAL OF HAZARDOUS MATERIALS 431.0(2022):128528. |
入库方式： OAI收割
来源：生态环境研究中心
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。