Structure Evolution and Properties Modification for Reaction-Bonded Silicon Carbide
文献类型：期刊论文
| 作者 | W. Li; G. Zhang; C. Cui; J. Bao; C. Guo; C. Xu; W. Zhang and W. Zhu |
| 刊名 | Materials
 |
| 出版日期 | 2022 |
| 卷号 | 15期号:24 |
| ISSN号 | 19961944 |
| DOI | 10.3390/ma15248721 |
| 英文摘要 | Complex structure reaction-bonded silicon carbide (RB-SiC) can be prepared by reactive melt infiltration (RMI) and digital light processing (DLP). However, the strength and modulus of RB-SiC prepared by DLP are not sufficient, due to its low solid content (around 40 vol.%), compared with the traditional fabrication techniques (solid content 60 vol.%). With this understanding, a new method to improve the properties of RB-SiC was proposed, by the impregnation of composite precursor into the porous preform. The composite precursor was composed of phenolic (PF) resin and furfuryl alcohol (FA). PF and FA were pyrolyzed at 1850 C to obtain amorphous carbon and graphite into the porous preform, respectively. The effects of multiphase carbon on the microstructure and performance of RB-SiC was studied. When the mass ratio of PF to FA was 1/4, the solid content of RB-SiC increased from 40 vol.% to 68.6 vol.%. The strength, bulk density and modulus were 323.12 MPa, 2.94 g/cm3 and 348.83 Gpa, respectively. This method demonstrated that the reaction process between liquid Si and carbon could be controlled by the introduction of multiphase carbon into the porous preforms, which has the potential to regulate the microstructure and properties of RB-SiC prepared by additive manufacturing or other forming methods. 2022 by the authors. |
| URL标识 | 查看原文 |
| 源URL | [http://ir.ciomp.ac.cn/handle/181722/67117]  |
| 专题 | 中国科学院长春光学精密机械与物理研究所 |
| 推荐引用方式 GB/T 7714 | W. Li,G. Zhang,C. Cui,et al. Structure Evolution and Properties Modification for Reaction-Bonded Silicon Carbide[J]. Materials,2022,15(24). |
| APA | W. Li.,G. Zhang.,C. Cui.,J. Bao.,C. Guo.,...&W. Zhang and W. Zhu.(2022).Structure Evolution and Properties Modification for Reaction-Bonded Silicon Carbide.Materials,15(24). |
| MLA | W. Li,et al."Structure Evolution and Properties Modification for Reaction-Bonded Silicon Carbide".Materials 15.24(2022). |
入库方式： OAI收割
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。