Self-supporting hierarchically-structured hollow ordered porous carbon spheres from spatially tangent compression
文献类型:会议论文
作者 | Wu, Xiao-Feng1; Cui, Yan-Bin1,2; Liao, Yu-Chao1,2; Chen, Yun-Fa1 |
出版日期 | 2013-02-01 |
关键词 | Mesoporous materials - X ray diffraction - Lithium batteries - Spheres - Carbon - Silica - Lithium |
卷号 | 13 |
期号 | 2 |
DOI | 10.1166/jnn.2013.5992 |
页码 | 1323-1326 |
英文摘要 | Self-supporting hierarchically-structured hollow ordered porous carbon spheres (HOPCSs) have been synthesized successfully using hollow ordered mesoporous silica spheres (HOMSSs) with MCM-41 pore structure within shells as templates. The SEM and TEM observations show that the final HOPCS product presents spherical morphology with hollow interiors. The results of HRTEM, small angle X-ray Diffraction (SAXRD) and N2 adsorption-desorption isotherms confirm that the HOPCS inversely replicate the MCM41 hexagonally-stacked ordered microstructures within shells and possess the ordered porosity. Furthermore, the formation of ordered porous structures within HOPCSs is due to the two aspects below: (i) the inverse carbonaceous replicas filling in hexagonally-stacked mesopores in HOMSSs are compacted tangentially due to curvature difference along the radial direction, self-supporting ordered porous structures after removing silica template; (ii) the additional carbon deposition layers exist on the outside surface of the replicas, cooperatively cementing the carbon fillers. Copyright 漏 2013 American Scientific Publishers All rights reserved. |
资助机构 | American Scientific Publishers |
学科主题 | Porosity |
源URL | [http://ir.ipe.ac.cn/handle/122111/59395] |
作者单位 | 1.State Key Laboratory of Multiphase Complex System, Institute of Process Engineering, Chinese Academy of Sciences, Beijing, 100190, China 2.Graduate University of Chinese Academy of Sciences, Beijing, 100049, China |
推荐引用方式 GB/T 7714 | Wu, Xiao-Feng,Cui, Yan-Bin,Liao, Yu-Chao,et al. Self-supporting hierarchically-structured hollow ordered porous carbon spheres from spatially tangent compression[C]. 见:. |