Influence of Al addition on the grain boundary oxidation of ultra high strength steels during hot coiling
文献类型：期刊论文
| 作者 | Liu, Zihe1,2; Yang, Xiaoguang1; Mao, Weichen3,4; Jin, Xinyan3,4; Wang, Li3,4; Zhang, Xue1,2; Li, Ying1,2 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2023-02-01 |
| 卷号 | 211页码:9 |
| ISSN号 | 0010-938X |
| 关键词 | A Alloy B XPS TEM C High temperature corrosion Selective oxidation Kinetic parameters |
| DOI | 10.1016/j.corsci.2022.110863 |
| 通讯作者 | Zhang, Xue(xuezhang@imr.ac.cn) |
| 英文摘要 | Ultra-high strength steel (UHSS) is the most attractive lightweight material for automotive industry. However, the formation of internal oxides especially along grain boundaries during coiling after hot rolling can signifi-cantly deteriorate the surface quality of the final product. Herein, we report the influence of Al addition on the internal oxidation of Fe-Mn-Si model alloys of UHSS. Experimental results show a significantly reduced inter -granular oxidation for the Al-containing alloys. The beneficial effects of Al are attributed to a modified oxygen activity condition at the scale/substrate interface and a rather depletion of reactant elements at grain boundaries. |
| 资助项目 | Natural Science Foun- dation of Liaoning, China ; [2022 -MS -015] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| WOS记录号 | WOS:000902662100001 |
| 资助机构 | Natural Science Foun- dation of Liaoning, China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/175739]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhang, Xue |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Baosteel Res Inst, Shanghai 201900, Peoples R China 4.Baosteel, State Key Lab Dev & Applicat Technol Automot Steel, Shanghai 201900, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu, Zihe,Yang, Xiaoguang,Mao, Weichen,et al. Influence of Al addition on the grain boundary oxidation of ultra high strength steels during hot coiling[J]. CORROSION SCIENCE,2023,211:9. |
| APA | Liu, Zihe.,Yang, Xiaoguang.,Mao, Weichen.,Jin, Xinyan.,Wang, Li.,...&Li, Ying.(2023).Influence of Al addition on the grain boundary oxidation of ultra high strength steels during hot coiling.CORROSION SCIENCE,211,9. |
| MLA | Liu, Zihe,et al."Influence of Al addition on the grain boundary oxidation of ultra high strength steels during hot coiling".CORROSION SCIENCE 211(2023):9. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。