Fretting corrosion-induced microstructural evolution of Alloy 690TT tube in high temperature pressurised water
文献类型：期刊论文
| 作者 | Zhang, Yusheng2,3; Wu, Bin2,3; Ming, Hongliang2,3; Li, Yifeng1; Zhang, Zhiming4; Wang, Jianqiu2,4; Han, En-Hou2,4 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2022-12-01 |
| 卷号 | 209页码:17 |
| 关键词 | Fretting corrosion Alloy 690TT High temperature pressurised water Oxidation Microstructure |
| ISSN号 | 0010-938X |
| DOI | 10.1016/j.corsci.2022.110774 |
| 通讯作者 | Ming, Hongliang(hlming12s@imr.ac.cn) ; Zhang, Zhiming(zmzhang@icost.ac.cn) |
| 英文摘要 | The friction-induced microstructural evolution of Alloy 690TT tubes submerged in a high temperature pres-surised water was investigated. Two typical local regions characterised by significantly different worn mor-phologies (resulting from the stress field and material couple) were investigated in detail. A thin third-body layer and a thick Fe-rich layer were observed and their oxidation behaviour was analysed. Moreover, the main oxide was spinel, whereas the amorphous band was only observed in the Fe-rich layer. The tribologically transformed structure is formed by the mechanism of discontinuous dynamic recrystallisation. Finally, the microstructural evolution of the two areas during fretting corrosion is discussed. |
| 资助项目 | National Natural Science Foundation of China[52105221] ; Youth Innovation Promotion Association CAS[2022187] ; IMR Innovation Fund[2021-PY10] ; CNNC Science Fund for Talented Young Scholars |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000884853500002 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 资助机构 | National Natural Science Foundation of China ; Youth Innovation Promotion Association CAS ; IMR Innovation Fund ; CNNC Science Fund for Talented Young Scholars |
| 源URL | [http://ir.imr.ac.cn/handle/321006/176746]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Ming, Hongliang; Zhang, Zhiming |
| 作者单位 | 1.Shanghai Univ, Instrumental Anal & Res Ctr, 99 Shangda Rd, Shanghai 200444, Peoples R China 2.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China 3.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 4.Inst Corros Sci & Technol, Guangzhou 510530, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, Yusheng,Wu, Bin,Ming, Hongliang,et al. Fretting corrosion-induced microstructural evolution of Alloy 690TT tube in high temperature pressurised water[J]. CORROSION SCIENCE,2022,209:17. |
| APA | Zhang, Yusheng.,Wu, Bin.,Ming, Hongliang.,Li, Yifeng.,Zhang, Zhiming.,...&Han, En-Hou.(2022).Fretting corrosion-induced microstructural evolution of Alloy 690TT tube in high temperature pressurised water.CORROSION SCIENCE,209,17. |
| MLA | Zhang, Yusheng,et al."Fretting corrosion-induced microstructural evolution of Alloy 690TT tube in high temperature pressurised water".CORROSION SCIENCE 209(2022):17. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。