Corrosion behaviors of FeCrAl alloys exposed to oxygen-saturated static lead bismuth eutectic at 550 degrees C
文献类型：期刊论文
| 作者 | Zhu, Zhaoguang1,2; Tan, Jibo1; Wu, Xinqiang1; Zhang, Ziyu1; Han, En-Hou1; Wang, Xiang1 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2022-12-01 |
| 卷号 | 209页码:15 |
| 关键词 | Alloy TEM Oxidation High temperature corrosion Thermodynamic diagrams |
| ISSN号 | 0010-938X |
| DOI | 10.1016/j.corsci.2022.110767 |
| 通讯作者 | Tan, Jibo(jbtan10s@imr.ac.cn) |
| 英文摘要 | The corrosion behaviors of two types of FeCrAl alloys were investigated in static oxygen-saturated lead bismuth eutectic (LBE) at 550 degrees C for up to 8000 h. It was found that the oxide film consists of plumboferrite, Fe3O4 and Fe-Cr-Al spinel. The thickness of the oxide film increased with increasing exposure time from 0 h to 4000 h, and then remained stable from 4000 h to 8000 h. Numerous layered Al-rich and Cr-rich spinel were observed in the Fe-Cr-Al spinel layer and layered alpha-Al2O3 was observed at the oxide/matrix interface. The corrosion mechanism of FeCrAl alloys in liquid LBE is discussed. |
| 资助项目 | Youth Innovation Promotion Association CAS[2021189] ; IMR (China) Innovation Fund[2021- PY01] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000884390000001 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 资助机构 | Youth Innovation Promotion Association CAS ; IMR (China) Innovation Fund |
| 源URL | [http://ir.imr.ac.cn/handle/321006/176783]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Tan, Jibo |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Mat, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhu, Zhaoguang,Tan, Jibo,Wu, Xinqiang,et al. Corrosion behaviors of FeCrAl alloys exposed to oxygen-saturated static lead bismuth eutectic at 550 degrees C[J]. CORROSION SCIENCE,2022,209:15. |
| APA | Zhu, Zhaoguang,Tan, Jibo,Wu, Xinqiang,Zhang, Ziyu,Han, En-Hou,&Wang, Xiang.(2022).Corrosion behaviors of FeCrAl alloys exposed to oxygen-saturated static lead bismuth eutectic at 550 degrees C.CORROSION SCIENCE,209,15. |
| MLA | Zhu, Zhaoguang,et al."Corrosion behaviors of FeCrAl alloys exposed to oxygen-saturated static lead bismuth eutectic at 550 degrees C".CORROSION SCIENCE 209(2022):15. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。