Effect of temperature on low cycle fatigue behavior of T91 steel in liquid lead-bismuth eutectic environment at 150-550 degrees C
文献类型：期刊论文
| 作者 | Xue, Baoquan1,2; Tan, Jibo1; Zhang, Ziyu1; Wang, Xiang1; Wu, Xinqiang1; Han, En-Hou1; Ke, Wei1 |
| 刊名 | INTERNATIONAL JOURNAL OF FATIGUE
 |
| 出版日期 | 2023-02-01 |
| 卷号 | 167页码:16 |
| ISSN号 | 0142-1123 |
| 关键词 | T91 steel Corrosion fatigue Liquid metal corrosion Liquid metal embrittlement |
| DOI | 10.1016/j.ijfatigue.2022.107344 |
| 通讯作者 | Tan, Jibo(jbtan10s@imr.ac.cn) |
| 英文摘要 | The low cycle fatigue behavior of T91 steel in a lead-bismuth eutectic and an air environment was investigated at 150-550 degrees C. The temperature dependent "fatigue endurance peak and trough" was found in liquid LBE. Quasi-cleavage cracking was observed on the fracture surface at 150 degrees C and 350 degrees C, which indicates the occurrence of liquid metal embrittlement (LME). The plasticity recovery reduced LME susceptibility of T91 steel at 250 degrees C and 550 degrees C. The effects of LME, liquid LBE corrosion and dynamic strain aging on the mechanisms of fatigue crack initiation and propagation are discussed. |
| 资助项目 | Youth Innovation Promotion Association CAS ; National Natural Science Foundation of China ; IMR Innovation Fund ; [2021189] ; [52271077] ; [2021-PY01] |
| WOS研究方向 | Engineering ; Materials Science |
| 语种 | 英语 |
| 出版者 | ELSEVIER SCI LTD |
| WOS记录号 | WOS:000892489800001 |
| 资助机构 | Youth Innovation Promotion Association CAS ; National Natural Science Foundation of China ; IMR Innovation Fund |
| 源URL | [http://ir.imr.ac.cn/handle/321006/176994]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Tan, Jibo |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Mat, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China |
| 推荐引用方式 GB/T 7714 | Xue, Baoquan,Tan, Jibo,Zhang, Ziyu,et al. Effect of temperature on low cycle fatigue behavior of T91 steel in liquid lead-bismuth eutectic environment at 150-550 degrees C[J]. INTERNATIONAL JOURNAL OF FATIGUE,2023,167:16. |
| APA | Xue, Baoquan.,Tan, Jibo.,Zhang, Ziyu.,Wang, Xiang.,Wu, Xinqiang.,...&Ke, Wei.(2023).Effect of temperature on low cycle fatigue behavior of T91 steel in liquid lead-bismuth eutectic environment at 150-550 degrees C.INTERNATIONAL JOURNAL OF FATIGUE,167,16. |
| MLA | Xue, Baoquan,et al."Effect of temperature on low cycle fatigue behavior of T91 steel in liquid lead-bismuth eutectic environment at 150-550 degrees C".INTERNATIONAL JOURNAL OF FATIGUE 167(2023):16. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。