The development of thermally stable sealing glass in the BaO-B(2)O(3)-SiO(2) system for planar SOFC applications
文献类型：期刊论文
| 作者 | Peng, Lian1,2; Zhu, Qingshan |
| 刊名 | JOURNAL OF FUEL CELL SCIENCE AND TECHNOLOGY
 |
| 出版日期 | 2008-08-01 |
| 卷号 | 5期号:3 |
| 关键词 | sealing glass coefficient of thermal expansion thermal stability SOFC |
| ISSN号 | 1550-624X |
| 其他题名 | J. Fuel Cell Sci. Technol. |
| 中文摘要 | The purpose of the present paper is to study the influence of glass composition on the thermal stability in the SiO(2)-B(2)O(3)-BaO system, and three glasses were consequently investigated. Although Glass A has a coefficient of thermal expansion (CTE) that shows the best match with those of anode and electrolyte materials of solid oxide fuel cells (SOFCs), the thermal stability of Glass A is quite poor where after being heat treated at 800 degrees C for only 8 h, the CTE of the glass increased more than 24%. Them change of the CTE value was mainly attributed to the fast crystallization that formed high CTE value phases such as BaB(2)O(4) and Ba(2)Si(3)O(8). In order to improve the thermal stability, BaO in Glass A was replaced by B(2)O(3) (Glass B) and SiO(2) (Glass C). It was found that the decrease in the BaO content improved the thermal stability of the resultant glasses. Glass B showed less than 8% change of the CTE during annealing time at 800 degrees C, while Glass C exhibited superior long-term. thermal stability, where the change of the CTE was within the equipment detection limit after being heat treated for 300 It at 800 degrees C. The good thermal stability of Glass C was believed to be due to the formation of a more compact glass network after the substitution as compared with that of Glass A. The good thermal. stability makes Glass C attractive to be used as the sealing material for SOFC applications. |
| 英文摘要 | The purpose of the present paper is to study the influence of glass composition on the thermal stability in the SiO(2)-B(2)O(3)-BaO system, and three glasses were consequently investigated. Although Glass A has a coefficient of thermal expansion (CTE) that shows the best match with those of anode and electrolyte materials of solid oxide fuel cells (SOFCs), the thermal stability of Glass A is quite poor where after being heat treated at 800 degrees C for only 8 h, the CTE of the glass increased more than 24%. Them change of the CTE value was mainly attributed to the fast crystallization that formed high CTE value phases such as BaB(2)O(4) and Ba(2)Si(3)O(8). In order to improve the thermal stability, BaO in Glass A was replaced by B(2)O(3) (Glass B) and SiO(2) (Glass C). It was found that the decrease in the BaO content improved the thermal stability of the resultant glasses. Glass B showed less than 8% change of the CTE during annealing time at 800 degrees C, while Glass C exhibited superior long-term. thermal stability, where the change of the CTE was within the equipment detection limit after being heat treated for 300 It at 800 degrees C. The good thermal stability of Glass C was believed to be due to the formation of a more compact glass network after the substitution as compared with that of Glass A. The good thermal. stability makes Glass C attractive to be used as the sealing material for SOFC applications. |
| WOS标题词 | Science & Technology ; Physical Sciences ; Technology |
| 类目[WOS] | Electrochemistry ; Energy & Fuels |
| 研究领域[WOS] | Electrochemistry ; Energy & Fuels |
| 关键词[WOS] | OXIDE FUEL-CELLS ; COMPOSITES ; BARIUM |
| 收录类别 | SCI ; ISTP |
| 原文出处 | |
| 语种 | 英语 |
| WOS记录号 | WOS:000257586400019 |
| 公开日期 | 2013-10-08 |
| 版本 | 出版稿 |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/2827]  |
| 专题 | 过程工程研究所_研究所（批量导入） |
| 作者单位 | 1.Chinese Acad Sci, Inst Proc Engn, State Key Lab Multiphase Complex Syst, Beijing 100190, Peoples R China 2.Chinese Acad Sci, Grad Univ, Beijing 100190, Peoples R China |
| 推荐引用方式 GB/T 7714 | Peng, Lian,Zhu, Qingshan. The development of thermally stable sealing glass in the BaO-B(2)O(3)-SiO(2) system for planar SOFC applications[J]. JOURNAL OF FUEL CELL SCIENCE AND TECHNOLOGY,2008,5(3). |
| APA | Peng, Lian,&Zhu, Qingshan.(2008).The development of thermally stable sealing glass in the BaO-B(2)O(3)-SiO(2) system for planar SOFC applications.JOURNAL OF FUEL CELL SCIENCE AND TECHNOLOGY,5(3). |
| MLA | Peng, Lian,et al."The development of thermally stable sealing glass in the BaO-B(2)O(3)-SiO(2) system for planar SOFC applications".JOURNAL OF FUEL CELL SCIENCE AND TECHNOLOGY 5.3(2008). |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。