Crack initiation and propagation of defects adjacent to the X65 pipeline spiral weld under axial tensile force
文献类型：期刊论文
| 作者 | Zhang, Dan; Zhu, Haohao; Zhang, Cheng; Wang, Jinchao; Guo, Hailin |
| 刊名 | INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING
 |
| 出版日期 | 2022-12-01 |
| 卷号 | 200 |
| ISSN号 | 0308-0161 |
| 关键词 | X65 pipeline Spiral weld Defect Wide plate tensile test Crack initiation and propagation |
| 英文摘要 | The pipeline structure is prone to fracture by the synergistic effect of external forces and defects, which may lead to disastrous consequences. Therefore, it is of great engineering significance to study the crack initiation and propagation of defected pipelines. In this study, a series of simulations and experiments based on the wide plate tensile test were carried out. The effects of the size and position parameters of the defects adjacent to the pipeline spiral weld on crack initiation and propagation were investigated. The simulation results show that the dimensions of a single defect affected the crack initiation and propagation. Besides, the experiment results show that the mutual influence on the crack initiation and propagation between two defects was related to the position and distance of the double-defect. Observations of the pipeline stress and strain revealed that compared with the centrosymmetric double-defect, the likelihood of the fracture of the pipeline with the axisymmetric double-defect increased when the distance between the two defects was the same. |
| 学科主题 | Engineering |
| 语种 | 英语 |
| 出版者 | ELSEVIER SCI LTD |
| WOS记录号 | WOS:000864862400004 |
| 源URL | [http://119.78.100.198/handle/2S6PX9GI/34893]  |
| 专题 | 中科院武汉岩土力学所 |
| 作者单位 | 1.China University of Geosciences; 2.Chinese Academy of Sciences; Wuhan Institute of Rock & Soil Mechanics, CAS |
| 推荐引用方式 GB/T 7714 | Zhang, Dan,Zhu, Haohao,Zhang, Cheng,et al. Crack initiation and propagation of defects adjacent to the X65 pipeline spiral weld under axial tensile force[J]. INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING,2022,200. |
| APA | Zhang, Dan,Zhu, Haohao,Zhang, Cheng,Wang, Jinchao,&Guo, Hailin.(2022).Crack initiation and propagation of defects adjacent to the X65 pipeline spiral weld under axial tensile force.INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING,200. |
| MLA | Zhang, Dan,et al."Crack initiation and propagation of defects adjacent to the X65 pipeline spiral weld under axial tensile force".INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING 200(2022). |
入库方式： OAI收割
来源：武汉岩土力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。