Cu-Y2O3 Catalyst Derived from Cu2Y2O5 Perovskite for Water Gas Shift Reaction: The Effect of Reduction Temperature
文献类型：期刊论文
| 作者 | Wang, Zeyu1,2; Luo, Fengying1,2; Wang, Nan1; Li, Xinjun1
|
| 刊名 | CATALYSTS
 |
| 出版日期 | 2022-05-01 |
| 卷号 | 12期号:5页码:14 |
| 关键词 | Cu2Y2O5 perovskite reduction temperature Cu-Y2O3 catalyst water gas shift reaction Cu degrees facet |
| DOI | 10.3390/catal12050481 |
| 通讯作者 | Li, Xinjun(lixj@ms.giec.ac.cn) |
| 英文摘要 | Cu2Y2O5 perovskite was reduced at different temperatures under H-2 atmosphere to prepare two Cu-Y2O3 catalysts. The results of the activity test indicated that the Cu-Y2O3 catalyst after H-2-reduction at 500 degrees C (RCYO-500) exhibited the best performance in the temperature range from 100 to 180 degrees C for water gas shift (WGS) reaction, with a CO conversion of 57.30% and H-2 production of 30.67 mu mol center dot g(cat)(-1)center dot min(-1) at 160 degrees C and a gas hourly space velocity (GHSV) of 6000 mL center dot g(cat)(-1)center dot h(-1). The catalyst reduced at 320 degrees C (RCYO-320) performed best at the temperature range from 180 to 250 degrees C, which achieved 86.44% CO conversion and 54.73 mu mol center dot g(cat)(-1)center dot min(-1) H-2 production at 250 degrees C. Both of the Cu-Y2O3 catalysts had similar structures including Cu degrees, Cu+, oxygen vacancies (Vo) on the Cu degrees-Cu+ interface and Y2O3 support. RCYO-500, with a mainly exposed Cu degrees (100) facet, was active in the low-temperature WGS reaction, while the WGS activity of RCYO-320, which mainly exposed the Cu degrees (111) facet, was greatly enhanced above 180 degrees C. Different Cu degrees facets have different abilities to absorb H2O and then dissociate it to form hydroxyl groups, which is the main step affecting the catalytic rate of the WGS reaction. |
| WOS关键词 | COPPER-CATALYSTS ; WGS REACTION ; METAL-OXIDE ; OPTIMIZATION ; MECHANISM ; SURFACES ; OXYGEN |
| 资助项目 | National Key R&D Program of China[2021YFC1910404] ; Natural Science Foundation of Guangdong Province, China[2021 A1515010445] ; Science and Technology Program of Guangzhou, China[202102020402] |
| WOS研究方向 | Chemistry |
| 语种 | 英语 |
| 出版者 | MDPI |
| WOS记录号 | WOS:000803603500001 |
| 资助机构 | National Key R&D Program of China ; Natural Science Foundation of Guangdong Province, China ; Science and Technology Program of Guangzhou, China |
| 源URL | [http://ir.giec.ac.cn/handle/344007/36665]  |
| 专题 | 中国科学院广州能源研究所 |
| 通讯作者 | Li, Xinjun |
| 作者单位 | 1.Chinese Acad Sci, Guangzhou Inst Energy Convers, Guangzhou 510640, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang, Zeyu,Luo, Fengying,Wang, Nan,et al. Cu-Y2O3 Catalyst Derived from Cu2Y2O5 Perovskite for Water Gas Shift Reaction: The Effect of Reduction Temperature[J]. CATALYSTS,2022,12(5):14. |
| APA | Wang, Zeyu,Luo, Fengying,Wang, Nan,&Li, Xinjun.(2022).Cu-Y2O3 Catalyst Derived from Cu2Y2O5 Perovskite for Water Gas Shift Reaction: The Effect of Reduction Temperature.CATALYSTS,12(5),14. |
| MLA | Wang, Zeyu,et al."Cu-Y2O3 Catalyst Derived from Cu2Y2O5 Perovskite for Water Gas Shift Reaction: The Effect of Reduction Temperature".CATALYSTS 12.5(2022):14. |
入库方式： OAI收割
来源：广州能源研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。