The influence of hydrogen permeation on the protection performance of the Cu coating of nuclear waste containers
文献类型：期刊论文
| 作者 | Liu, Xiangju1,3; Liu, Nazhen1,2,3; Noel, James J.; Shoesmith, David W.2; Chen, Jian2; Hou, Baorong1,3 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2023-08-15 |
| 卷号 | 221页码:12 |
| ISSN号 | 0010-938X |
| 关键词 | A. Metal coatings B. Hydrogen permeation B. Polarization C. Electrodeposited films |
| DOI | 10.1016/j.corsci.2023.111314 |
| 通讯作者 | Liu, Nazhen(liunazhen@qdio.ac.cn) |
| 英文摘要 | Hydrogen permeation and corrosion behaviour of Cu-coated carbon steel under simulated nuclear waste disposal conditions of the Beishan area have been investigated. The permeation current (with 500 mu A center dot cm(-2) charging current) decreased from 3778 to 141 and 47 nA.cm(-2) respectively when 5 and 10 mu m thick Cu coatings were electrodeposited on the steel. The XRD analysis suggests the formation of CuH during the hydrogen charging treatment, and its subsequent decomposition formed a protective CuOH/Cu2O layer on the charging surface when exposed to simulated groundwater for 44 h. No damage to the Cu coating-steel interface was observed in the cross-section analysis. |
| WOS关键词 | CALCAREOUS DEPOSITS ; FILM GROWTH ; CORROSION BEHAVIOR ; GALVANIC CORROSION ; COPPER HYDRIDE ; CARBON-STEEL ; EMBRITTLEMENT ; SULFIDE ; ABSORPTION ; ADSORPTION |
| 资助项目 | National Natural Science Foundation of China[51901222] ; National Natural Science Foundation of China[41827805] ; CAS Pioneer Hundred Talents Program |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| WOS记录号 | WOS:001024736700001 |
| 源URL | [http://ir.qdio.ac.cn/handle/337002/182619]  |
| 专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
| 通讯作者 | Liu, Nazhen |
| 作者单位 | 1.Pilot Natl Lab Marine Sci & Technol Qingdao, Open Studio Marine Corros & Protect, Qingdao 266237, Peoples R China 2.Western Univ, Chem Dept, London, ON N6A 5B7, Canada 3.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu, Xiangju,Liu, Nazhen,Noel, James J.,et al. The influence of hydrogen permeation on the protection performance of the Cu coating of nuclear waste containers[J]. CORROSION SCIENCE,2023,221:12. |
| APA | Liu, Xiangju,Liu, Nazhen,Noel, James J.,Shoesmith, David W.,Chen, Jian,&Hou, Baorong.(2023).The influence of hydrogen permeation on the protection performance of the Cu coating of nuclear waste containers.CORROSION SCIENCE,221,12. |
| MLA | Liu, Xiangju,et al."The influence of hydrogen permeation on the protection performance of the Cu coating of nuclear waste containers".CORROSION SCIENCE 221(2023):12. |
入库方式： OAI收割
来源：海洋研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。