High-cycle and very-high-cycle fatigue of an additively manufactured aluminium alloy under axial cycling at ultrasonic and conventional frequencies
文献类型：期刊论文
| 作者 | Pan XN(潘向南) ; Hong YS(洪友士)
|
| 刊名 | INTERNATIONAL JOURNAL OF FATIGUE
 |
| 出版日期 | 2024-08-01 |
| 卷号 | 185页码:13 |
| 关键词 | Very -high -cycle fatigue (VHCF) Loading frequency Mean stress Aluminium alloy Additive manufacturing |
| ISSN号 | 0142-1123 |
| DOI | 10.1016/j.ijfatigue.2024.108363 |
| 通讯作者 | Pan, Xiangnan(panxiangnan@lnm.imech.ac.cn) ; Hong, Youshi(hongys@imech.ac.cn) |
| 英文摘要 | Along the building direction, the fatigue behavior of an additively manufactured (AM) aluminium (AlSi10Mg) alloy was investigated in high-cycle and very-high-cycle regimes by using conventionally electromagnetic resonance and ultrasonic vibration with axial loading frequencies of -110 Hz and -20 k +/- 500 Hz, respectively. No frequency effect was observed on the resulted fatigue strength and the fractography up to 108 cycles at stress ratio R = -1. All cracks initiated at AM pores and the dominating one prefers shifting from specimen surface to subsurface with growing very-high-cycle fatigue (VHCF) lives. As the tensile mean stress increases, fatigue strength sharply drops in high value regime of R >= 0.5 with annihilating VHCF occurrence, and the fatigue limits degrade on a Gerber relation beyond 109 cycles. At last, a fatigue failure map was proposed to directly describe the panorama of specimen lives under different external loads. |
| 分类号 | 一类 |
| WOS关键词 | SLM ALSI10MG SPECIMENS ; CHROMIUM-BEARING STEEL ; CRACK INITIATION ; VHCF RESPONSE ; EARLY GROWTH ; BEHAVIOR ; STRENGTH ; STRESS ; LIFE ; MECHANISM |
| 资助项目 | National Natural Science Foundation of China[11932020] |
| WOS研究方向 | Engineering ; Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:001238414100001 |
| 资助机构 | National Natural Science Foundation of China |
| 其他责任者 | Pan, Xiangnan ; Hong, Youshi |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/95581]  |
| 专题 | 力学研究所_非线性力学国家重点实验室 |
| 推荐引用方式 GB/T 7714 | Pan XN,Hong YS. High-cycle and very-high-cycle fatigue of an additively manufactured aluminium alloy under axial cycling at ultrasonic and conventional frequencies[J]. INTERNATIONAL JOURNAL OF FATIGUE,2024,185:13. |
| APA | 潘向南,&洪友士.(2024).High-cycle and very-high-cycle fatigue of an additively manufactured aluminium alloy under axial cycling at ultrasonic and conventional frequencies.INTERNATIONAL JOURNAL OF FATIGUE,185,13. |
| MLA | 潘向南,et al."High-cycle and very-high-cycle fatigue of an additively manufactured aluminium alloy under axial cycling at ultrasonic and conventional frequencies".INTERNATIONAL JOURNAL OF FATIGUE 185(2024):13. |
入库方式： OAI收割
来源：力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。