The stacking fault annihilation in a-plane AlN during high-temperature annealing
文献类型：期刊论文
| 作者 | X. Sun, J. Sui, J. Ben, H. Zang, K. Jiang, S. Zhang, S. Lv, Z. Shi, T. Wu and D. Li |
| 刊名 | CrystEngComm
 |
| 出版日期 | 2023 |
| 卷号 | 25期号:13页码:1903-1909 |
| ISSN号 | 14668033 |
| DOI | 10.1039/d2ce01654k |
| 英文摘要 | Clarifying the defect evolution mechanism is the key to realizing high-quality non-polar AlN based materials and devices. In this work, the basal stacking fault density of the sputtered nonpolar a-plane wurtzite AlN (a-AlN) template decreased from 27 100 cm−1 to 5500 cm−1 by high-temperature annealing and the underlying mechanism is systematically investigated by first-principle calculations. By analysing the minimum energy pathway during the elimination of the I1-type stacking fault, it was found that two I1-type stacking faults transform into one I3-type stacking fault as the intermediate state and then annihilate. The highest energy barriers for eliminating and forming the I1-type stacking default are 5.032 eV and 5.204 eV, respectively, explaining the phenomenon that the BSFD decreases at first and then increases with the increasing annealing temperature. In addition, the FWHMs of (11−20) XRC along different azimuth angles are nearly uniform instead of the normal ‘M’ shape, indicating that the crystal quality of a-AlN improved uniformly along different azimuth angles after high-temperature annealing. The results presented here are a significant step towards the synthesis of high-quality non-polar AlN material and non-polar light-emitting diodes. © 2023 The Royal Society of Chemistry. |
| URL标识 | 查看原文 |
| 源URL | [http://ir.ciomp.ac.cn/handle/181722/67872]  |
| 专题 | 中国科学院长春光学精密机械与物理研究所 |
| 推荐引用方式 GB/T 7714 | X. Sun, J. Sui, J. Ben, H. Zang, K. Jiang, S. Zhang, S. Lv, Z. Shi, T. Wu and D. Li. The stacking fault annihilation in a-plane AlN during high-temperature annealing[J]. CrystEngComm,2023,25(13):1903-1909. |
| APA | X. Sun, J. Sui, J. Ben, H. Zang, K. Jiang, S. Zhang, S. Lv, Z. Shi, T. Wu and D. Li.(2023).The stacking fault annihilation in a-plane AlN during high-temperature annealing.CrystEngComm,25(13),1903-1909. |
| MLA | X. Sun, J. Sui, J. Ben, H. Zang, K. Jiang, S. Zhang, S. Lv, Z. Shi, T. Wu and D. Li."The stacking fault annihilation in a-plane AlN during high-temperature annealing".CrystEngComm 25.13(2023):1903-1909. |
入库方式： OAI收割
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。