The effect of NaCl-induced corrosion on Ti60′s hot salt stress corrosion cracking
文献类型：期刊论文
| 作者 | Chen, Wenzheng1; Wang, Wenquan1; Liu, Li1; Liu, Rui1; Cui, Yu2; Chen, Zhiyong2; Wang, Qingjiang2; Wang, Fuhui1 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2024 |
| 卷号 | 226页码:17 |
| 关键词 | Titanium Alloy Stress-corrosion cracking High temperature corrosion TEM |
| ISSN号 | 0010-938X |
| DOI | 10.1016/j.corsci.2023.111677 |
| 通讯作者 | Liu, Li(liuli@mail.neu.edu.cn) |
| 英文摘要 | The hot salt stress corrosion cracking (HSSCC) behaviour of Ti60 alloy at 600 degrees C in moist air has been studied, focusing on NaCl-induced corrosion as an embrittlement mechanism. NaCl-induced active corrosion was proven to happen at the crack front. This corrosion process promoted the loss of metal and the ingress of O, leading to quick O embrittlement of the alloy. In the alloy, the beta phase can somewhat inhibit HSSCC due to its less sensitivity to corrosion-promoted O ingress. Phase boundaries have strong corrosion sensitivity to NaCl-induced corrosion. Thus, phase boundaries are prone to cracking. |
| 资助项目 | National Natural Science Foundation of China[52301082] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001119262000001 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/177129]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Liu, Li |
| 作者单位 | 1.Northeastern Univ, Shenyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China 2.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Wenhua Rd 72, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Chen, Wenzheng,Wang, Wenquan,Liu, Li,et al. The effect of NaCl-induced corrosion on Ti60′s hot salt stress corrosion cracking[J]. CORROSION SCIENCE,2024,226:17. |
| APA | Chen, Wenzheng.,Wang, Wenquan.,Liu, Li.,Liu, Rui.,Cui, Yu.,...&Wang, Fuhui.(2024).The effect of NaCl-induced corrosion on Ti60′s hot salt stress corrosion cracking.CORROSION SCIENCE,226,17. |
| MLA | Chen, Wenzheng,et al."The effect of NaCl-induced corrosion on Ti60′s hot salt stress corrosion cracking".CORROSION SCIENCE 226(2024):17. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。