In vitro degradation, wear property and biocompatibility of nano-Y2O3-containing micro-arc oxidation coating on ZK60 alloy
文献类型：期刊论文
| 作者 | Chen, Jun-xiu2,3; Yang, Yang2,3; Etim, Iniobong P.4; Tan, Li -li4; Yang, Ke4; Misra, R. D. K.1; Wang, Jian-hua2,3; Su, Xu-ping2,3 |
| 刊名 | TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
 |
| 出版日期 | 2023-05-01 |
| 卷号 | 33期号:5页码:1411-1424 |
| 关键词 | MAO coating wear property degradation resistance biocompatibility |
| ISSN号 | 1003-6326 |
| DOI | 10.1016/S1003-6326(23)66192-8 |
| 通讯作者 | Chen, Jun-xiu(czdxcjx@cczu.edu.cn) ; Su, Xu-ping(sxping@cczu.edu.cn) |
| 英文摘要 | In order to further improve the degradation resistance and wear property of micro-arc oxidation (MAO) coating on magnesium alloys, nano-Y2O3 was added into the electrolyte to fabricate a nano-Y2O3-containing MAO coating. Microstructural characterization, wear test, electrochemical test, immersion test and cytotoxicity test were carried out. The results showed that there were mainly Ca8MgY(PO4)7 and Y2O3 particles in the MAO coating. Ca8MgY(PO4)7 could stabilize the coating and the nano-Y2O3 could seal the micro-pores. Therefore, both the degradation resistance and wear property of the coating were improved. The degradation rate decreased from 0.14 to 0.06 mm/a in Hank's solution. The volume loss decreased from 0.46 to 0.27 mm3 at the same slip distance. MAO coating exhibited good biocompatibility with the cell relative growth rate (RGR) value of more than 90%. The nano-Y2O3-containing MAO coating thus has a good promising biomedical application. |
| 资助项目 | National Natural Science Foundation of China[52001034] ; National Natural Science Foundation of China[51871030] ; Changzhou Sci & Tech Program, China[CJ20200078] ; Natural Science Foundation of Jiangsu Higher Education Institutions of China[20KJB430013] ; Top-notch Academic Programs of Jiangsu Higher Education Institutions, China (TAPP) ; Priority Academic Program Development of Jiangsu Higher Education Institutions, China (PAPD) |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001100450800001 |
| 出版者 | ELSEVIER |
| 资助机构 | National Natural Science Foundation of China ; Changzhou Sci & Tech Program, China ; Natural Science Foundation of Jiangsu Higher Education Institutions of China ; Top-notch Academic Programs of Jiangsu Higher Education Institutions, China (TAPP) ; Priority Academic Program Development of Jiangsu Higher Education Institutions, China (PAPD) |
| 源URL | [http://ir.imr.ac.cn/handle/321006/177536]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Chen, Jun-xiu; Su, Xu-ping |
| 作者单位 | 1.Univ Texas, Dept Met Mat & Biomed Engn, El Paso, TX 79968 USA 2.Changzhou Univ, Jiangsu Collaborat Innovat Ctr Photovolta Sci & En, Changzhou 213164, Jiangsu, Peoples R China 3.Changzhou Univ, Key Lab Mat Surface Sci & Technol Jiangsu Prov, Changzhou 213164, Peoples R China 4.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Chen, Jun-xiu,Yang, Yang,Etim, Iniobong P.,et al. In vitro degradation, wear property and biocompatibility of nano-Y2O3-containing micro-arc oxidation coating on ZK60 alloy[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2023,33(5):1411-1424. |
| APA | Chen, Jun-xiu.,Yang, Yang.,Etim, Iniobong P..,Tan, Li -li.,Yang, Ke.,...&Su, Xu-ping.(2023).In vitro degradation, wear property and biocompatibility of nano-Y2O3-containing micro-arc oxidation coating on ZK60 alloy.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,33(5),1411-1424. |
| MLA | Chen, Jun-xiu,et al."In vitro degradation, wear property and biocompatibility of nano-Y2O3-containing micro-arc oxidation coating on ZK60 alloy".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 33.5(2023):1411-1424. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。