Corrosion Evolution of Nickel Aluminum Bronze in Clean and Sulfide-Polluted Solutions
文献类型：期刊论文
| 作者 | Yang, Liu1,2; Wei, Yinghua2 |
| 刊名 | COATINGS
 |
| 出版日期 | 2023-04-28 |
| 卷号 | 13期号:5页码:17 |
| 关键词 | nickel aluminum bronze SVET corrosion evolution sulfide |
| DOI | 10.3390/coatings13050846 |
| 通讯作者 | Wei, Yinghua(yhwei@imr.ac.cn) |
| 英文摘要 | Nickel aluminum bronze (NAB) alloys are reported to suffer accelerated local corrosion in sulfide-polluted seawater. In this work, the real-time in situ scanning vibrating electrode technique (SVET) was employed to monitor the evolution of the corrosion product film of a typical NAB alloy immersed in the clean and sulfide-polluted 3.5% NaCl solutions. In the sulfide-free condition, the corrosion current peak surged at the individual point of the NAB surface and receded to calm in 2 h. In the presence of the sulfide, however, multiple active points on the measured metal surface released high corrosion current for a long time, indicating that intense corrosion had occurred. The corrosion mass loss was more than four times the former. Global electrochemical techniques, scanning electron microscopy (SEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) were adopted to perform a comprehensive analysis of the composition of the corrosion product films. The results show that a dense layer of aluminum and cuprous oxide forms on the NAB surface in the sulfide-free solution, while a loose mixture of cuprous sulfide and cuprous oxide is detected in the sulfide-contaminated solution. This finding is believed to account for the observed distinction between the corrosion behavior of NAB in the two solutions. |
| 资助项目 | Strategic Precursor Research Program of the Chinese Academy of Sciences[XDA 13040501] |
| WOS研究方向 | Materials Science ; Physics |
| 语种 | 英语 |
| WOS记录号 | WOS:000997316000001 |
| 出版者 | MDPI |
| 资助机构 | Strategic Precursor Research Program of the Chinese Academy of Sciences |
| 源URL | [http://ir.imr.ac.cn/handle/321006/177965]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wei, Yinghua |
| 作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 230026, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yang, Liu,Wei, Yinghua. Corrosion Evolution of Nickel Aluminum Bronze in Clean and Sulfide-Polluted Solutions[J]. COATINGS,2023,13(5):17. |
| APA | Yang, Liu,&Wei, Yinghua.(2023).Corrosion Evolution of Nickel Aluminum Bronze in Clean and Sulfide-Polluted Solutions.COATINGS,13(5),17. |
| MLA | Yang, Liu,et al."Corrosion Evolution of Nickel Aluminum Bronze in Clean and Sulfide-Polluted Solutions".COATINGS 13.5(2023):17. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。