Corrosion evolution of high-temperature formed oxide film on pure Sn solder substrate
文献类型：期刊论文
| 作者 | Zhao, Hui3; Sun, Xu3,4; Hao, Long1,4; Wang, Jian-qiu1,4; Yang, Jing-mei2 |
| 刊名 | TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
 |
| 出版日期 | 2022-12-01 |
| 卷号 | 32期号:12页码:3998-4013 |
| 关键词 | pure Sn solder oxide film high-temperature aging corrosion resistance |
| ISSN号 | 1003-6326 |
| DOI | 10.1016/S1003-6326(22)66073-4 |
| 通讯作者 | Hao, Long(chinahaolong@126.com) |
| 英文摘要 | The evolution of morphology, composition, thickness and corrosion resistance of the oxide film on pure Sn solder substrate submitted to high-temperature aging in 150 degrees C dry atmosphere was investigated. The results indicate that high-temperature aging accelerates the dehydration of Sn(OH)(4) in the pre-existing native oxide film to form SnO2 and facilitates the oxidation of fresh Sn substrate, resulting in the gradual increase in oxide film thickness and surface roughness with prolonging aging time. However, the corrosion resistance of the film initially is enhanced and then deteriorated with an extending aging time. Besides, the formation and evolution mechanisms of the oxide film with aging time were discussed. |
| 资助项目 | CAS Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000988117800012 |
| 出版者 | ELSEVIER |
| 资助机构 | CAS Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences |
| 源URL | [http://ir.imr.ac.cn/handle/321006/177976]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Hao, Long |
| 作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China 2.Shenyang Aircraft Ind Grp Corp Ltd, Shenyang 110034, Peoples R China 3.Shenyang Ligong Univ, Sch Mat Sci & Engn, Shenyang 110159, Peoples R China 4.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhao, Hui,Sun, Xu,Hao, Long,et al. Corrosion evolution of high-temperature formed oxide film on pure Sn solder substrate[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2022,32(12):3998-4013. |
| APA | Zhao, Hui,Sun, Xu,Hao, Long,Wang, Jian-qiu,&Yang, Jing-mei.(2022).Corrosion evolution of high-temperature formed oxide film on pure Sn solder substrate.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,32(12),3998-4013. |
| MLA | Zhao, Hui,et al."Corrosion evolution of high-temperature formed oxide film on pure Sn solder substrate".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 32.12(2022):3998-4013. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。