Process Parameter Optimization for the Laser Metal Deposition of a Functionally Graded GH4169/K417G Superalloy and the Effects of Preheating and Composition on Cracking Behavior
文献类型：期刊论文
| 作者 | Liu, Shuai2; Liu, Changsheng1; Yuan, Chao2 |
| 刊名 | JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
 |
| 出版日期 | 2023-07-05 |
| 页码 | 17 |
| 关键词 | cracking functionally graded material (FGM) laser metal deposition (LMD) process parameter optimization superalloys |
| ISSN号 | 1059-9495 |
| DOI | 10.1007/s11665-023-08376-5 |
| 通讯作者 | Liu, Shuai(15040369625@163.com) ; Liu, Changsheng(csliu@mail.neu.edu.cn) ; Yuan, Chao(ychao@imr.ac.cn) |
| 英文摘要 | This study aims to select a suitable process and composition for the fabrication of a functionally graded GH4169/K417G superalloy by laser metal deposition (LMD). A universal process parameter was optimized through an orthogonal test, and the influence of the preheated substrate temperature on the residual stress was investigated. Finally, the effects of preheating and composition on cracking and methods for controlling cracking were noted. As a result, equations for the relationship between the relative densities of samples prepared by LMD with different graded compositions and energy density coupled to laser parameters were established for the first time. Thus, an equation for the relationship between the appropriate laser power and graded composition was obtained. By preheating the substrate to higher temperatures, the maximum residual stress was gradually reduced from 753 to 362 MPa, and thus, the cracking tendency was suppressed partly. However, the decisive cracking factor was the & gamma;/& gamma;& PRIME; eutectic characteristic during the forming of K417G. When the terminal graded composition was designed to be 10% GH4169, the & gamma;/& gamma;& PRIME; eutectic phase exhibited a smaller size and lower quantity, which prevented cracking. The results of this research will help engineers select the appropriate compositions and processes to prepare dual-superalloy blisks. |
| 资助项目 | Joint Founds of National Natural Science Foundation of China (NSFC)-Liaoning[U1508213] ; Liaoning Provincial Natural Science Foundation of China[2020-KF-14-02] ; Opening Project of State Key Laboratory of Light Alloy Casting Technology for High-end Equipment[LACT-008] |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:001022635100004 |
| 出版者 | SPRINGER |
| 资助机构 | Joint Founds of National Natural Science Foundation of China (NSFC)-Liaoning ; Liaoning Provincial Natural Science Foundation of China ; Opening Project of State Key Laboratory of Light Alloy Casting Technology for High-end Equipment |
| 源URL | [http://ir.imr.ac.cn/handle/321006/178483]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Liu, Shuai; Liu, Changsheng; Yuan, Chao |
| 作者单位 | 1.Northeastern Univ, Sch Mat Sci & Engn, Key Lab Anisotropy & Texture Mat, Minist Educ, Shenyang 110819, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu, Shuai,Liu, Changsheng,Yuan, Chao. Process Parameter Optimization for the Laser Metal Deposition of a Functionally Graded GH4169/K417G Superalloy and the Effects of Preheating and Composition on Cracking Behavior[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,2023:17. |
| APA | Liu, Shuai,Liu, Changsheng,&Yuan, Chao.(2023).Process Parameter Optimization for the Laser Metal Deposition of a Functionally Graded GH4169/K417G Superalloy and the Effects of Preheating and Composition on Cracking Behavior.JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,17. |
| MLA | Liu, Shuai,et al."Process Parameter Optimization for the Laser Metal Deposition of a Functionally Graded GH4169/K417G Superalloy and the Effects of Preheating and Composition on Cracking Behavior".JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE (2023):17. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。