Effect of Residual Stress on Reheat Cracking Susceptibility of Super304H Austenitic Stainless Steel Weld Metal
文献类型：期刊论文
| 作者 | Xiao Xiaopeng1,3; Dong Wenchao3; Li Dianzhong3; Li Yiyi2,3; Lu Shanping3 |
| 刊名 | RARE METAL MATERIALS AND ENGINEERING
 |
| 出版日期 | 2023-06-01 |
| 卷号 | 52期号:6页码:2093-2102 |
| 关键词 | reheat cracking residual stress austenitic stainless steel weld metal dislocation density |
| ISSN号 | 1875-5372 |
| 通讯作者 | Lu Shanping(shplu@imr.ac.cn) |
| 英文摘要 | The effect of residual stress on the reheat cracking susceptibility of Super304H austenitic stainless steel weld metal by the pre-compressed CT specimen method was studied. The plastic strain and dislocation density distribution of weld metal under different residual stresses were analyzed by ABAQUS simulation combined with EBSD characterization. The effect of residual stress on the reheat cracking susceptibility was explained from the aspect of stress-induced precipitation. The results show that CT specimens with high pre-compression force have higher residual stress and are more likely to generate cracks. With increasing the residual stress, the tensile strength of the specimen is decreased gradually. The high residual stress region of the CT specimen closed to the U-shaped notch has higher dislocation density and subgrain, promoting the precipitation of the small intragranular phase, which makes the intragranular hardening more serious and the easy occurrence of reheat cracks. |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001028537300010 |
| 出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
| 源URL | [http://ir.imr.ac.cn/handle/321006/178789]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Lu Shanping |
| 作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China 3.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Xiao Xiaopeng,Dong Wenchao,Li Dianzhong,et al. Effect of Residual Stress on Reheat Cracking Susceptibility of Super304H Austenitic Stainless Steel Weld Metal[J]. RARE METAL MATERIALS AND ENGINEERING,2023,52(6):2093-2102. |
| APA | Xiao Xiaopeng,Dong Wenchao,Li Dianzhong,Li Yiyi,&Lu Shanping.(2023).Effect of Residual Stress on Reheat Cracking Susceptibility of Super304H Austenitic Stainless Steel Weld Metal.RARE METAL MATERIALS AND ENGINEERING,52(6),2093-2102. |
| MLA | Xiao Xiaopeng,et al."Effect of Residual Stress on Reheat Cracking Susceptibility of Super304H Austenitic Stainless Steel Weld Metal".RARE METAL MATERIALS AND ENGINEERING 52.6(2023):2093-2102. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。